Using piezoelectric diagnostics, we have measured densities and velocities of ejected particulate as well as "free-surface velocities" of bulk tin targets shock loaded with high explosive. The targets had finely grooved, machined finishes ranging from 10 to 250 in. Two types of piezoelectric sensor ͑"piezopins"͒, lithium niobate and lead zirconate titanate, were compared for durability and repeatability; in addition, some piezopins were "shielded" with foam and metal foil in order to mitigate premature failure of the pins in high ejecta regimes. These experiments address questions about ejecta production at a given shock pressure as a function of surface finish; piezopin results are compared with those from complementary diagnostics such as x-ray radiography and time-resolved optical transmission techniques. The mass ejection shows a marked dependence on groove characteristics and cannot be described by a groove defect theory alone.

We have assembled together our ejecta measurements from explosively shocked tin acquired over a period of about ten years. The tin was cast at 0.99995 purity, and all of the tin targets or samples were shocked to loading pressures of about 27 GPa, allowing meaningful comparisons. The collected data are markedly consistent, and because the total ejected mass scales linearly with the perturbations amplitudes they can be used to estimate how much total Sn mass will be ejected from explosively shocked Sn, at similar loading pressures, based on the surface perturbation parameters of wavelength and amplitude. Most of the data were collected from periodic isosceles shapes that approximate sinusoidal perturbations. Importantly, however, we find that not all periodic perturbations behave similarly. For example, we observed that sawtooth (right triangular) perturbations eject more mass than an isosceles perturbation of similar depth and wavelength, demonstrating that masses ejected from irregular shaped perturbations cannot be normalized to the cross-sectional areas of the perturbations.

This effort investigates the underlying physics of ejecta production for high explosive (HE) shocked Sn surfaces prepared with finishes typical to those roughened by tool marks left from machining processes. To investigate the physical mechanisms of ejecta production, we compiled and re-examined ejecta data from two experimental campaigns [W. S. Vogan et al., J. Appl. Phys. 98, 113508 (1998); M. B. Zellner et al., ibid. 102, 013522 (2007)] to form a self-consistent data set spanning a large parameter space. In the first campaign, ejecta created upon shock release at the back side of HE shocked Sn samples were characterized for samples with varying surface finishes but at similar shock-breakout pressures PSB. In the second campaign, ejecta were characterized for HE shocked Sn samples with a constant surface finish but at varying PSB.