Fe3Al-based iron aluminides have been of interest for many years because of their excellent oxidation and sulfidation resistance. However, limited room temperature ductility (<5%) and a sharp drop in strength above 600 °C have limited their consideration for use as structural materials. Recent improvements in tensile properties, especially improvements in ductility produced through control of composition and microstructure, and advances in the understanding of environmental embrittlement in intermetallics, including iron aluminides, have resulted in renewed interest in this system for structural applications. The purpose of this paper is to summarize recent developments concerning Fe3Al-based aluminides, including alloy development efforts and environmental embrittlement studies. This report will concentrate on literature published since about 1980, and will review studies of fabrication, mechanical properties, and corrosion resistance that have been conducted since that time.
MoSi2 is a promising high-temperature material with low density (6.3 g/cm3), high melting point (2020 °C), and good oxidation resistance at temperatures to about 1900 °C. However, in the intermediate temperature range between 400 and 600 °C, it is susceptible to a “pest” reaction which causes catastrophic disintegration by a combination of oxidation and fracture. In this study, we have used polycrystalline MoSi2, produced by arc-casting of the pure elements and by cold and hot pressing of alloy powders, to characterize the pest reaction and to determine the roles of composition, grain or phase boundaries, and physical defects on the oxidation and fracture of specimens exposed to air at 500 °C. It was found that pest disintegration occurs through transport of oxygen into the interior of the specimen along pre-existing cracks and/or pores, where it reacts to form MoO3 and SiO2. The internal stress produced during the formation of MoO3 results in disintegration to powder. Near the stoichiometric ratio, the susceptibility to pest disintegration increases with increasing molybdenum content and with decreasing density. Silicon-rich alloys were able to form protective SiO2 and showed no indication of disintegration, even at densities as low as 60%.
NOTICE This document contains information of a preliminary nature. I t is subject to revision or correction and therefore does not represent a final report.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.