Abstract--Samples of nacrite, dickite, kaolinite, and halloysite were investigated using X-band electron paramagnetic resonance (EPR) and Mbssbauer spectroscopy. Fe 3+ gave rise to EPR signals at g = 4 which differed with the individual polytype. Only nacrite had no resonance in this region of the spectrum, but it had one at g ~ 2. Dickite had a quadruple line, kaolinite a triple line, and halloysite a single line in this region. The EPR spectra of these minerals are apparently dependent also on the orientation of adjacent layers in the structures. Other resonances were attributed to (1) clusters of ferric ions giving rise to broad resonance near g = 2, (2) trapped holes, and (3) free radicals linked with organic matter. The Mbssbauer spectroscopic results suggest that iron occurs in the ferric state (except in nacrite where Fe 2+ is present also) as an ionic substitution (IS) in octahedral layers. This suggestion follows from the difference is the IS values between octahedral and tetrahedral symmetry sites occupied by Fe a+ equal to -0.4 mm/sec. Linewidths depend mainly on the way the layers stack; for monoclinic modifications represented by nacrite and dickite, the linewidths are narrow (F = 0.45 mm/sec and 0.56 mm/sec, respectively); pseudomonoclinic halloysites also gave narrow linewidths (F = 0.39 mm/sec and 0.48 mm/sec). The widest line was observed for triclinic kaolinite (F = 0.62 mm/sec and 0.71 mm/sec).

No abstract