INGENIERIE+SAG:YSC:DFAThe number and strength of adsorption sites for Xe in silver-modified zeolites are estimated from isotherm measurements at various temperatures over a broad range of pressure (from 1 ppm to atmospheric pressure). Fully and partially exchanged silver zeolites were synthesized starting from Na-ZSM-5(25), Na-ZSM-5(40), Na-Beta, NaX, and NaY. We have discovered that silver-modified zeolites may present one or two distinct adsorption sites depending on the nature of the material and silver loadings. The strongest adsorption sites are characterized by isosteric heat of adsorption in the order of -40 to -50 kJ.mol(-1). For Pentasil-type zeolites, we observe a linear 2:1 correlation between the total amount of silver and the number of strong sites. The highest concentration of strong sites is found for fully silver exchanged ZSM-5 (5.7 X 10(-4) mol/g), which presents the largest silver content for Pentasil-type zeolite. The equilibrium constant of Ag-ZSM-5 at low pressure is about 50 times larger than that of AgX. Qualitative correlations were established between Xe adsorption isotherms and Xe NMR signals. We show that Xe NMR could be used as a quantitative method for the characterization of the strength and of the number of strong Xe adsorption sites on silver-exchanged zeolites. The numbers of strong adsorption sites responsible for the Xe adsorption at 10-1000 ppm can be determined by the length of the plateau observed at low Xe uptake. In practice, our findings give guidelines for the discovery and optimization of silver-loaded zeolites for the capture of Xe at ppm levels. It appears that the amount of silver is a key parameter. Silver-modified ZSM-5 shows adsorption capacities 2-3 orders of magnitude larger than currently applied adsorbents for atmospheric Xe capture

International audienceMolecular simulation is used to unravel the adsorption mechanisms of xenon on Ag-doped ZSM-5 zeolite. We show that silver nanoparticles, which form at the external surface of zeolite crystallites, are responsible for enhanced xenon physisorption at very low pressure. We also propose a simple model of adsorption on such composite materials made up of silver-exchanged zeolites and silver nanoparticles adsorbed at the zeolite surface. This model, which allows predicting the adsorption of other gases without any additional parameters, provides a tool to characterize the amount of reduced silver as well as the silver particle size distribution (in good agreement with transmission electron microscopy images). The presence of a majority of silver nanoparticles is further characterized by means of X-ray diffraction and X-ray Absorption Spectroscopy at the silver K edge