Ternary Ag-In-S or quaternary Ag-In-Zn-S nanocrystals were prepared from simple precursors (silver nitrate, indium(iii) chloride, zinc stearate in a mixture of DDT and ODE) by injecting a solution of elemental sulfur into OLA. Ternary nanocrystals were modified by depositing either a ZnS or a CdS shell, yielding type I and type II core/shell systems exhibiting photoluminescence QY in the range of 12-16%. Careful optimization of the reaction conditions allowed alloyed quaternary Ag-In-Zn-S nanocrystals exhibiting tunable photoluminescence in the spectral range of 520-720 nm with a QY of 48% and 59% for green and red radiations, respectively, to be obtained. H NMR analysis of the nanocrystal organic shell, after dissolution of its inorganic core, indicated that surfacial sulfur atoms were covalently bonded to aliphatic chains whereas surfacial cations were coordinated by amines and carboxylate anions. No thiol-type ligands were detected. Transfer of the prepared nanocrystals to water could be achieved in one step by exchanging the initial ligands for 11-mercaptoundecanoic ones resulting in a QY value of 31%. A new Ag-In-Zn-S nanocrystal preparation method was elaborated in which indium and zinc salts of fatty acids were used as cation precursors and DDT was replaced by thioacetamide. This original DDT-free method enabled similar tuning of the photoluminescence properties of the nanocrystals as in the previous method; however the measured photoluminescence QYs were three times lower. Hence, further optimization of the new method is required.

A new indium precursor, namely, indium(II) chloride, was tested as a precursor in the synthesis of ternary Ag−In−S and quaternary Ag−In−Zn−S nanocrystals. This new precursor, being in fact a dimer of Cl 2 In−InCl 2 chemical structure, is significantly more reactive than InCl 3 , typically used in the preparation of these types of nanocrystals. This was evidenced by carrying out comparative syntheses under the same reaction conditions using these two indium precursors in combination with the same silver (AgNO 3 ) and zinc (zinc stearate) precursors. In particular, the use of indium(II) chloride in combination with low concentrations of the zinc precursor yielded spherical-shaped (D = 3.7−6.2 nm) Ag−In−Zn−S nanocrystals, whereas for higher concentrations of this precursor, rodlike nanoparticles (L = 9−10 nm) were obtained. In all cases, the resulting nanocrystals were enriched in indium (In/Ag = 1.5−10.3). Enhanced indium precursor conversion and formation of anisotropic, longitudinal nanoparticles were closely related to the presence of thiocarboxylic acid type of ligands in the reaction mixture. These ligands were generated in situ and subsequently bound to surfacial In(III) cations in the growing nanocrystals. The use of the new precursor of enhanced reactivity facilitated precise tuning of the photoluminescence color of the resulting nanocrystals in the spectral range from ca. 730 to 530 nm with photoluminescence quantum yield (PLQY) varying from 20 to 40%. The fabricated Ag−In−S and Ag−In−Zn−S nanocrystals exhibited the longest, reported to date, photoluminescence lifetimes of ∼9.4 and ∼1.4 μs, respectively. It was also demonstrated for the first time that ternary (Ag−In− S) and quaternary (Ag−In−Zn−S) nanocrystals could be applied as efficient photocatalysts, active under visible light (green) illumination, in the reaction of aldehydes reduction to alcohols.