Biodegradable composite materials can be produced by the combination of biodegradable polymers and natural fibers. In this study, a new biodegradable composite of hemp fiber reinforced polylactic acid (PLA) was fabricated using the hot press method. Mechanical properties of composites with different fiber volume fractions were tested. The optimum fiber content was determined according to the test results. Effects of alkali treatment on the fiber surface morphology and the mechanical properties of the composites were investigated. Test results show that the composite with 40% volume fraction of alkali treated fiber has the best mechanical properties. The tensile strength, elastic modulus, and flexural strength of the composite with 40% treated fiber are 54.6 MPa, 8.5 Gpa, and 112.7 MPa respectively, which are much higher than those of PLA alone. The composites have lower densities, which were measured to be from 1.19 g/cm 3 to 1.25 g/cm 3 . Specific strengths were also calculated. Surface morphologies of fiber and fracture surfaces of the composites were observed using the SEM method.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.