Attempts at depositing uniform films of nanoparticles by drop-drying have been frustrated by the "coffee-stain" effect due to convective macroscopic flow into the contact line. Here, we show that uniform deposition of nanoparticles in aqueous suspensions can be attained easily by drying the droplet in an ethanol vapor atmosphere. This technique allows the particle-laden water droplets to spread on a variety of surfaces such as glass, silicon, mica, PDMS, and even Teflon. Visualization of droplet shape and internal flow shows initial droplet spreading and strong recirculating flow during spreading and shrinkage. The initial spreading is due to a diminishing contact angle from the absorption of ethanol from the vapor at the contact line. During the drying phase, the vapor is saturated in ethanol, leading to preferential evaporation of water at the contact line. This generates a surface tension gradient that drives a strong recirculating flow and homogenizes the nanoparticle concentration. We show that this method can be used for depositing catalyst nanoparticles for the growth of single-walled carbon nanotubes as well as to manufacture plasmonic films of well-spaced, unaggregated gold nanoparticles.

We demonstrate continuous roll-to-roll production of highly conductive silver network films on a plastic substrate via mechanical and chemical welding processes. This process included three essential steps: (i) solvent spraying, (ii) roll compression, and (iii) salt treatment and washing. The sheet resistance of the resulting AgNW film was 5 Ω sq(-1) at 92% transmittance, which was the lowest sheet resistance and the highest transparency among the values reported previously for solution-processed AgNW electrodes. Moreover, the strong contacts among the AgNWs dramatically enhanced the mechanical stability of the network film. The resulting AgNW film was successfully applied to various organic electronic devices, such as organic field-effect transistors (OFETs), organic light-emitting diodes (OLEDs), and organic solar cells (OSCs).

Here, we design and develop high-power electric double-layer capacitors (EDLCs) using carbon-based three dimensional (3-D) hybrid nanostructured electrodes. 3-D hybrid nanostructured electrodes consisting of vertically aligned carbon nanotubes (CNTs) on highly porous carbon nanocups (CNCs) were synthesized by a combination of anodization and chemical vapor deposition techniques. A 3-D electrode-based supercapacitor showed enhanced areal capacitance by accommodating more charges in a given footprint area than that of a conventional CNC-based device.

Using the first-principles calculations, we explored the feasibility of using graphdiyne, a 2D layer of sp and sp2 hybrid carbon networks, as lithium ion battery anodes. We found that the composite of the Li-intercalated multilayer α-graphdiyne was C6Li7.31 and that the calculated voltage was suitable for the anode. The practical specific/volumetric capacities can reach up to 2719 mAh g−1/2032 mAh cm−3, much greater than the values of ∼372 mAh g−1/∼818 mAh cm−3, ∼1117 mAh g−1/∼1589 mAh cm−3, and ∼744 mAh g−1 for graphite, graphynes, and γ-graphdiyne, respectively. Our calculations suggest that multilayer α-graphdiyne can serve as a promising high-capacity lithium ion battery anode.

Heterostructures of compositionally and electronically variant two-dimensional (2D) atomic layers are viable building blocks for ultrathin optoelectronic devices. We show that the composition of interfacial transition region between semiconducting WSe2 atomic layer channels and metallic NbSe2 contact layers can be engineered through interfacial doping with Nb atoms. WxNb1-xSe2 interfacial regions considerably lower the potential barrier height of the junction, significantly improving the performance of the corresponding WSe2-based field-effect transistor devices. The creation of such alloyed 2D junctions between dissimilar atomic layer domains could be the most important factor in controlling the electronic properties of 2D junctions and the design and fabrication of 2D atomic layer devices.