An innovative and environmentally friendly method for the synthesis of size-controlled silver nanoparticles (AgNPs) is presented. Pectin-stabilized AgNPs were synthesized in a plasma-reaction system in which pulse-modulated radio-frequency atmospheric-pressure glow discharge (pm-rf-APGD) was operated in contact with a flowing liquid electrode. The use of pm-rf-APGD allows for better control of the size of AgNPs and their stability and monodispersity. AgNPs synthesized under defined operating conditions exhibited average sizes of 41.62 ± 12.08 nm and 10.38 ± 4.56 nm, as determined by dynamic light scattering and transmission electron microscopy (TEM), respectively. Energy-dispersive X-ray spectroscopy (EDS) confirmed that the nanoparticles were composed of metallic Ag. Furthermore, the ξ-potential of the AgNPs was shown to be −43.11 ± 0.96 mV, which will facilitate their application in biological systems. Between 70% and 90% of the cancerous cells of the human melanoma Hs 294T cell line underwent necrosis following treatment with the synthesized AgNPs. Furthermore, optical emission spectrometry (OES) identified reactive species, such as NO, NH, N2, O, and H, as pm-rf-APGD produced compounds that may be involved in the reduction of the Ag(I) ions.

Microwave treatment can reduce the time of selected syntheses, for instance of gold nanoparticles (AuNPs), from several hours to a few minutes. We propose a microfluidic structure for enhancing the rate of chemical reactions using microwave energy. This reactor is designed to control microwave energy with much higher accuracy than in standard devices. Thanks to this, the influence of microwave irradiation on the rate of chemical reactions can be investigated. The reactor consists of a transmission line surrounded by ground metallization. In order to deliver microwave energy to the fluid under test efficiently, matching networks are used and optimized by means of numerical methods. The monolithic device is fabricated in the low temperature co-fired ceramics (LTCC) technology. This material exhibits excellent microwave performance and is resistant to many chemical substances as well as high temperatures. Fabrication of the devices is described in detail. Measurements of microwave parameters are performed and differences between simulation and experiment results are discussed. Finally, the usefulness of the proposed device is proved in exemplary synthesis.

No abstract