The photovoltaic effects of blending gold nanoparticles (AuNPs) into the donor layer of a poly(3-hexylthiophene) (P3HT)/TiO2 bilayer heterojunction device have been studied. P3HT was synthesized via the modified Gragnard metathesis method and AuNPs with sizes ranging from 12 to 15 nm were formed via a reduction of HAuCl4. The blending of AuNPs into P3HT caused a lower photoluminescence (PL) intensities and a decreased energy level of the highest occupied molecular orbital (HOMO) than the pristine P3HT owing to the good electron-accepting nature of AuNPs. Upon the use of P3HT-AuNPs as the donor layer, the decreased HOMO(donor) resulted in an increased open circuit voltage (V(OC)) and thus enabled the fabricated (P3HT-AuNPs)/TiO2 bilayer heterojunction photovoltaic device to have an improved power conversion efficiency of solar energy. V(OC) as well as the overall power conversion efficiency increased with an increase in the AuNP content as a result of additional interfaces which facilitated the charge separation of excitons and percolation pathways which enhanced the electron transfer to the TiO2 acceptor. Furthermore, unannealed P3HT-AuNPs exhibited nanoholes and provided photovoltaic devices a power conversion efficiency nearly two time higher than annealed P3HT-AuNPs.

SiO2nanoparticles have been dispersed selectively in the polystyrene (PS) microdomain of polystyrene-block-polymethylmethacrylate (PS-b-PMMA) block copolymer via the blending of PS-b-PMMA with PS-tethered SiO2. As observed by atomic force microscopy and scanning electron microscopy, the incorporation of SiO2particles not only enlarges the PS microdomain but also reduces the surface energy of the PS microdomain and transforms the morphology from either lamellar layers or cylinders to islanded bicontinuous microstructures. Blending SiO2particles with an excessive amount or with a particle size larger than that of the PS microdomain would pose an extreme constraint on the molecular rearrangement, unstabliize the microdomain separation, and even make the microdomain separation unobservable. The nanosize and the uniform distribution of the PS microdomain in the PS-b-PMMA polymer have thus enabled us to achieve a uniform distribution of the inorganic SiO2particles in the organic polymeric matrix.

A novel conjugated block copolymer, poly(9,9-dioctylfluorene)-block-poly(3-hexylthiophene) (PFBPT) and its nanocomposite containing graphene sheets were synthesized for enhancing optoelectronic performance. Graphene sheets were in-situ formed in the polymer matrix via a reduction of octadecylamine-functionalized graphite oxide, where the graphite oxide came from acidification and exfoliation of graphite. The blue-green light-emitting poly(9,9-dioctylfluorene) block and red-orange light-emitting poly(3-hexylthiophene) block exhibit a combined white electroluminescence when the composite materials were fabricated as the emitting layer of a polymeric light-emitting diode (PLED). Graphene does not alter the optical characteristics wavelength of PFBPT but electric conductivity increases with the amount of graphene. The HOMO and LUMO were measured and the band gap is smaller with existence of graphene. The threshold voltage decreases with an increase in the graphene content. The device fabricated with PFBPT/graphene nanocomposite containing 1% graphene has a maximum white-light luminescence at a voltage of 9.0 V.

An effective method to synthesize directly a hard composite material containing uniformly dispersed nanogold particles chemically bonded with a stereospecific, crystalline polymer matrix has been developed. Syndiotactic polypropylene was synthesized and functionalized to have a hydroxyl terminal group (sPPOH) via a metallocene catalysis with a selective chain transfer. Next, sPPOH was activated to react with ethylene sulfide forming the thiol‐terminated polymer, sPPSH. sPPSH was then chemically bonded to gold nanoparticles (AuNPs) formed in situ via a reduction of HAuCl4. The bonding between thiol and AuNP stabilized the AuNPs and led to the formation of sPPAuNPs composite containing uniformly‐dispersed AuNPs of a 19–40 nm size without noticeable aggregation. Furthermore, the chemical bonding of AuNPs has afforded sPPAuNPs a thermal degradation temperature (TD) 49.4 °C higher than the pristine sPP or sPPOH and 25.7 °C higher than sPPSH without any adverse effect on the crystalline temperature and melting temperature. In addition, the characteristic UV‐Vis absorption wavelength of sPPAuNPs remains the same at various temperatures, thus indicating the independence of optical property on temperature as well as the good thermal stability of the sPPAuNPs composite. 1H NMR, 13C NMR, FESEM, STEM, XPS, TGA and DSC were used to investigate the molecular structure, morphology and thermal properties of the resulting sPPAuNPs nanocomposite. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2010

Hydroxyethyl-terminated poly(3-hexylthiophene) (P3HT-OH) have been synthesized via a catalyst-transfer polycondensation using Grignard metathesis mediated by a nickel-based catalyst. This hydrophilic P3HT-OH is compared against the hydrophobic P3HT when used as an active layer on silicon dioxide (SiO2) wafer for organic thin-film-transistor (OTFT) fabrication. Hydroxyl groups at a 7.5% weight content lead to more chain regularity when polymer is bonded to SiO2 wafer surface and thus enhance the performance of OTFT Device, such as an 114.2% increase in ON/OFF ratio, an 12.4% increase in mobility, a 23.3% decrease in threshold voltage and a 30.1% decrease in surface roughness. Analysis and measurements reported in this paper have illustrated for the first time the feasibility of imparting hydrophilicity to the active layer for improving the OTFT performance.