This is the author manuscript accepted for publication and has undergone full peer review but has not been through the copyediting, typesetting, pagination and proofreading process, which may lead to differences between this version and the Version of Record. Please cite this article as

Bismuth vanadate (BiVO4) is a promising photoelectrode material for the oxidation of water, but fundamental studies of this material are lacking. To address this, we report electrical and photoelectrochemical (PEC) properties of BiVO4 single crystals (undoped, 0.6% Mo, and 0.3% W:BiVO4) grown using the floating zone technique. We demonstrate that a small polaron hopping conduction mechanism dominates from 250 to 400 K, undergoing a transition to a variable-range hopping mechanism at lower temperatures. An anisotropy ratio of ~3 was observed along the c axis, attributed to the layered structure of BiVO4. Measurements of the ac field Hall effect yielded an electron mobility of ~0.2 cm(2) V(-1) s(-1) for Mo and W:BiVO4 at 300 K. By application of the Gärtner model, a hole diffusion length of ~100 nm was estimated. As a result of low carrier mobility, attempts to measure the dc Hall effect were unsuccessful. Analyses of the Raman spectra showed that Mo and W substituted for V and acted as donor impurities. Mott-Schottky analysis of electrodes with the (001) face exposed yielded a flat band potential of 0.03-0.08 V versus the reversible H2 electrode, while incident photon conversion efficiency tests showed that the dark coloration of the doped single crystals did not result in additional photocurrent. Comparison of these intrinsic properties to those of other metal oxides for PEC applications gives valuable insight into this material as a photoanode.

We demonstrate that solution-sequential processing (SqP) can yield heavily doped pristine-quality films when used to infiltrate the molecular dopant 2,3,5,6-tetrafluoro-7,7,8,8-tetracyanoquinodimethane (F4TCNQ) into pure poly(3-hexylthiophene) (P3HT) polymer layers. Profilometry measurements show that the SqP method produces doped films with essentially the same surface roughness as pristine films, and 2-D grazing-incidence wide-angle X-ray scattering (GIWAXS) confirms that SqP preserves both the size and orientation of the pristine polymer's crystallites. Unlike traditional blend-cast F4TCNQ/P3HT doped films, our sequentially processed layers have tunable and reproducible conductivities reaching as high as 5.5 S/cm even when measured over macroscopic (>1 cm) distances. The high conductivity and superb film quality allow for meaningful Hall effect measurements, which reveal p-type conduction and carrier concentrations tunable from 10(16) to 10(20) cm(-3) and hole mobilities ranging from ∼0.003 to 0.02 cm(2) V(-1) s(-1) at room temperature over the doping levels examined.

One of the most effective ways to tune the electronic properties of conjugated polymers is to dope them with small-molecule oxidizing agents, creating holes on the polymer and molecular anions. Undesirably, strong electrostatic attraction from the anions of most dopants localize the holes created on the polymer, reducing their mobility. Here, we employ a new strategy utilizing a substituted boron cluster as a molecular dopant for conjugated polymers. By designing the cluster to have a high redox potential and steric protection of the corelocalized electron density, we obtain highly delocalized polarons with mobilities equivalent to films doped with no anions present. AC Hall effect measurements show that P3HT films doped with our boron clusters have conductivities and polaron mobilities roughly an order of magnitude higher than films doped with F 4 TCNQ, even though the boron-cluster-doped films have poor crystallinity. Moreover, the number of free carriers approximately matches the number of boron clusters, yielding a doping efficiency of ∼100%. These results suggest that shielding the polaron from the anion is a critically important aspect for producing high carrier mobility, and that the high polymer crystallinity required with dopants such as F 4 TCNQ is primarily to keep the counterions far from the polymer backbone.

No abstract