The dynamic changes of the friction properties of the oxide film are characterized by the dynamic changes of the ELID grinding force. The tangential force and normal force are used to represent the friction coefficient in order to obtain the accurate real-time friction coefficient of oxide film. Therefore, the friction coefficient of various grinding wheels with different bonding agents, various grinding parameters, various grinding materials (nano- Al2O3 ceramic, nano ZrO2 ceramic and ordinary ZrO2 ceramic), and ELID grinding and ordinary grinding can be further studied. The results show that: the friction coefficient of the oxide film on the bronze-based grinding wheel is greater than that composed by iron; the friction coefficient of the oxide film decreases with the increase in grinding depth and feeding speed; the friction coefficient of the oxide film and nano-materials is smaller than that of the oxide film and ordinary materials; the transformation from γ-Fe2O3 to α-Fe2O3 in oxide film and the elastic deformation of the oxide film caused by the high-temperature of grinding may make the friction coefficient of ELID grinding greater than that of ordinary grinding, so the oxide film contains better property of friction and polishing. Therefore, excellent surface quality is easier to be obtained by it compared with the ordinary grinding technology.

The adhesion property of oxide film has great effects on the grinding quality and efficiency of ELID grinding. In this paper, adhesion strength model of oxide film is established, ELID grinding is conducted to nanometric cemented carbide and ordinary cemented carbide, ELID grinding force is measured, adhesive stress is calculated and the correctness of adhesion model is verified. The results show that the adhesion strength of oxide film is relatively greater, the transition from γ-Fe2O3to α-Fe2O3in the oxide film is relatively fuller and the polishing performance is relatively better while the grinding depth is smaller; with the deepening of grinding, the adhesion strength of oxide film reduces, the composition of the oxide film that transforms into α-Fe2O3is less and the polishing ability reduces. The adhesion model of oxide film well reflects the adhesion property of oxide film, and the application of this model can represent the distribution, shedding and updating of the oxide film on the surface of grinding wheel.

No abstract

This paper presents the study of forming mechanism of [Formula: see text]-Fe2O3 in oxide films on electrolytic in-process dressing (ELID) grinding wheel surface. To investigate the component content and the microtopography of oxide films, XRD, XPS, IR spectrum analysis, SEM, and TEM measurements are performed on ELID grinding wheels. In XRD test results, the characteristic absorption band of [Formula: see text]-Fe2O3 is found in the oxide film. XPS tests show that there is full of ferrous iron and oxygen element in the oxide film. Also, the characteristic spectral line of XPS is identical to the standard spectrum of [Formula: see text]-Fe2O3. Several vibration peaks (471, 1029, 1384, 1630, 3430) are observed by IR spectrum analysis. It can be easily seen by contrast with the standard photographs that the vibration peak of 1029 is of Fe-O vibration band in IR spectrum of [Formula: see text]-Fe2O3 powder. Therefore, these measurement results confirm the existence of [Formula: see text]-Fe2O3 in the oxide films, and explain the polishing effect of oxide films during ELID grinding. The fresh oxide film is porous and moisture rich. However, the oxide film after squeezing to dry is investigated by SEM imaging to present tortoiseshell cracks. Geometrically, [Formula: see text]-Fe2O3 appears to be nearly spherical with particle size around 5–50 nm. This indicates fine polishing improvement by oxide films, and is identified as the mechanism responsible for excellent surface quality by ELID grinding.

As the grain size of nano ceramic has reached nanometer grade, it possesses high hardness, high wear resistance and high toughness. Therefore, the scalpel made by nano ceramic has the virtue of high wear resistance, good corrosion resistance, long service life, non-toxic, non-static, sharp edge and so on, but the processing of this kind of scalpel is extremely difficult. This paper prepares the nano-ceramic scalpel by using ELID grinding technology, and also studies the thickness, surface roughness, edge sharpness of scalpel. The research results show that the thickness of prepared scalpel is 0.3 mm, the surface roughness is 6-60 nm and the edge radius is 200 nm, the cutting experiment on suture shows that this scalpel can meet the requirements of international standard for medical scalpel when the cutting force is less than 0.8 N. This further proves that the ELID grinding technology is suitable for the preparation of nano-ceramic scalpel. The preparation technology and technological equipment of nano-ceramic scalpel are proposed on the basis of above achievements, and this technology possesses promising application prospect.