No abstract

The environmentally friendly surfactant ethoxylated cardanol (EC) was investigated for dispersing copper phthalocyanine (CuPc) pigment nanoparticles into aqueous solution. The stability of the dispersion was investigated using UV-Vis spectra. The particle size was measured by optical microscopy, transmission electron microscopy and dynamic light scattering. The surface of the nanoparticles was characterised by measurements of the zeta potential and wettability. The coating application was investigated by incorporating CuPc blue pigment into resin and inorganic filler, and the colour strength of the coating film was compared. The results show that the EC can effectively wet and disperse the CuPc particles. The stabilisation of the particles is achieved by a steric mechanism in which the hydrophobic chains of the surfactant are adsorbed onto the surfaces of the CuPc nanoparticles and the ethylene oxide chains are dispersed in the aqueous phase. At EC concentrations greater than 0.1%, the CuPc nanoparticles appear to deagglomerate. The colour strength of CuPc nanoparticles present as dispersed pigment in resin can be increased in the presence of the EC surfactant.

In this study, an effective and environmentally friendly polyaminated cross-linked chitosan (M-PACTS) flocculant was successfully synthesized via circular focus single-mode microwave synthesizer irradiation. Epichlorohydrin and tetraethylenepentamine were used as the cross-linking agent and active cationic reagent, respectively. The same formation was used to prepare cationic lightly cross-linked chitosan (C-PACTS) via the conventional heating method. The flocculant was characterized using Fourier transform infrared spectroscopy, X-ray diffraction analysis, and scanning electron microscopy. The flocculation capability of C-PACTS and M-PACTS was compared using laundry wastewater as a model pollutant. The pH, PACTS dosage, temperature, stirring rate, stirring time, and setting time were systematically investigated. The experimental results showed that circular focus single-mode microwave synthesizer irradiation was a more efficient method to modify chitosan. M-PACTS exhibited a higher capacity for turbidity and chemical oxygen demand (COD Cr ) removal. Under optimal conditions, the removal rate values of M-PACTS were up to 96% (turbidity) and 78% (COD Cr ). The proposed PACTS is suitable for treatment of polluted wastewater in an eco-friendly manner without causing secondary pollution.

Low porosity and permeability of oil and gas reservoirs make it difficult to develop these resources. To address these problems, we developed and evaluated a novel, environmentally friendly waterproof locking agent, which was prepared using dimethyl silicone oil and octadecyltrimethylammonium chloride and characterized by Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, and particle size measurement. The waterproof locking performance of the agent was evaluated in a low-permeability reservoir using surface tension and contact angle measurements, and thermodynamic calculations were performed. The average particle size or median diameter ( D 50 ) of a 1% mother liquor was 325 nm at 20 °C and 470.8 nm at 70 °C. The contact angle of clean water on the core surface increased from 10 to 110°. At 70 °C, the surface tension of water was reduced to 24 mN·m –1 , indicating good waterproof locking performance. The interaction parameters were calculated in accordance with the Langmuir adsorption theory. The increase in temperature from 20 to 70 °C reduced Γ max from 4.59 × 10 –6 to 1.36 × 10 –6 mol·m –2 and Δ G θ from −40.93 to −56.54 kJ·mol –1 . Thus, the adsorption behavior of the developed locking agent is believed to improve the productivity of oil wells.