The mechanical properties of the 1-9 vol % Cu and Cu6Sn5-dispersed 63Sn-37Pb solder alloys were characterized with tensile test. Also, the Cu and Cu6Sn5-dispersed 63Sn-37Pb solder bumps of 760 μm size were fabricated on the Au(5 μm)/Ni(5 μm)/Cu(27 μm) BGA substrates by screen printing process, and their shear strength were characterized with variations of the dwell time at the reflow peak temperature(220°C) and aging time at 150°C. The yield strength and ultimate tensile strength of the 63Sn-37Pb solder alloy increased with dispersion of 1-9 vol % Cu and Cu6Sn5. In general, however, the Cu and Cu6Sn5-dispersed solder bumps exhibited lower shear strengths than those of the 63Sn-37Pb solder bumps The failure surface of the solder bumps after ball shear test could be divided into two regions of slow crack propagation and critical crack propagation, and the shear strength of solder bumps was inversely proportional to the slow crack propagation length.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.