In this work, novel high-strength, low-activation Wx(TaVZr)100−x (x = 5, 10, 15, 20, 25) refractory high entropy alloys (RHEAs) were prepared by vacuum arc melting. Their microstructure, compressive mechanical properties, hardness, and fracture morphology were investigated and analyzed. The results show that the RHEAs possess a disordered BCC phase, ordered Laves phase, and Zr-rich HCP phase. Their dendrite structures were observed, and the distribution of dendrites became gradually more dense with an increase in W content. The RHEAs demonstrate high strength and hardness, with these properties being higher than in most reported tungsten-containing RHEAs. For example, the typical W20(TaVZr)80 RHEA has a yield strength of 1985 MPa and a hardness of 636 HV, respectively. The improvement in terms of strength and hardness are mainly due to solid solution strengthening and the increase in dendritic regions. During compression, with the increase in the applied load, the fracture behavior of RHEAs changed from initial intergranular fractures to a mixed mode combining both intergranular and transgranular fractures.

During the past decade, refractory high-entropy alloys (RHEA) have attracted great attention of scientists, engineers and scholars due to their excellent mechanical and functional properties. The W-containing RHEAs are favored by researchers because of their great application potential in aerospace, marine and nuclear equipment and other high-temperature, corrosive and irradiated fields. In this review, more than 150 W-containing RHEAs are summarized and compared. The preparation techniques, microstructure and mechanical properties of the W-containing RHEAs are systematically outlined. In addition, the functional properties of W-containing RHEAs, such as oxidation, corrosion, irradiation and wear resistance have been elaborated and analyzed. Finally, the key issues faced by the development of W-containing RHEAs in terms of design and fabrication techniques, strengthening and deformation mechanisms, and potential functional applications are proposed and discussed. Future directions for the investigation and application of W-containing RHEAs are also suggested. The present work provides useful guidance for the development, processing and application of W-containing RHEAs and the RHEA components.