The development of new glassy materials is key for addressing major global challenges in energy, medicine, and advanced communications systems. For example, thin, flexible, and large-area glass substrates will play an enabling role in the development of flexible displays, roll-to-roll processing of solar cells, next-generation touch-screen devices, and encapsulation of organic semiconductors. The main drawback of glass and its limitation for these applications is its brittle fracture behavior, especially in the presence of surface flaws, which can significantly reduce the practical strength of a glass product. Hence, the design of new ultrastrong glassy materials and strengthening techniques is of crucial importance. The main issues regarding glass strength are discussed, with an emphasis on the underlying microscopic mechanisms that are responsible for mechanical properties. The relationship among elastic properties and fracture behavior is also addressed, focusing on both oxide and metallic glasses. From a theoretical perspective, atomistic modeling of mechanical properties of glassy materials is considered. The topological origin of these properties is also discussed, including its relation to structural and chemical heterogeneities. Finally, comments are given on several toughening strategies for increasing the damage resistance of glass products.
It is known that the coordination number (CN) of atoms or ions in many materials increases through application of sufficiently high pressure. This also applies to glassy materials. In boron-containing glasses, trigonal BO3 units can be transformed into tetrahedral BO4 under pressure. However, one of the key questions is whether the pressure-quenched CN change in glass is reversible upon annealing below the ambient glass transition temperature (Tg). Here we address this issue by performing 11B NMR measurements on a soda lime borate glass that has been pressure-quenched at ~0.6 GPa near Tg. The results show a remarkable phenomenon, i.e., upon annealing at 0.9Tg the pressure-induced change in CN remains unchanged, while the pressurised values of macroscopic properties such as density, refractive index, and hardness are relaxing. This suggests that the pressure-induced changes in macroscopic properties of soda lime borate glasses compressed up to ~0.6 GPa are not attributed to changes in the short-range order in the glass, but rather to changes in overall atomic packing density and medium-range structures.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.