Mechano-biochemical wear encompasses the tribological interplay between biological and mechanical mechanisms responsible for cartilage wear and degradation. The aim of this study was to develop and start validating a novel tribological testing system, which better resembles the natural joint environment through incorporating a live cartilage-on-cartilage articulating interface, joint specific kinematics, and the application of controlled mechanical stimuli for the measurement of biological responses in order to study the mechano-biochemical wear of cartilage. The study entailed two parts. In Part 1, the novel testing rig was used to compare two bearing systems: (a) cartilage articulating against cartilage (CoC) and (b) metal articulating against cartilage (MoC). The clinically relevant MoC, which is also a common tribological interface for evaluating cartilage wear, should produce more wear to agree with clinical observations. In Part II, the novel testing system was used to determine how wear is affected by tissue viability in live and dead CoC articulations. For both parts, bovine cartilage explants were harvested and tribologically tested for three consecutive days. Wear was defined as release of glycosaminoglycans into the media and as evaluation of the tissue structure. For Part I, we found that the live CoC articulation did not cause damage to the cartilage, to the extent of being comparable to the free swelling controls, whereas the MoC articulation caused decreased cell viability, extracellular matrix disruption, and increased wear when compared to CoC, and consistent with clinical data. These results provided confidence that this novel testing system will be adequate to screen new biomaterials for articulation against cartilage, such as in hemiarthroplasty. For Part II, the live and dead cartilage articulation yielded similar wear as determined by the release of proteoglycans and aggrecan fragments, suggesting that keeping the cartilage alive may not be essential for short term wear tests. However, the biosynthesis of glycosaminoglycans was significantly higher due to live CoC articulation than due to the corresponding live free swelling controls, indicating that articulation stimulated cell activity. Moving forward, the cell response to mechanical stimuli and the underlying mechano-biochemical wear mechanisms need to be further studied for a complete picture of tissue degradation.

There is a need for a simple method to control fluid flow within microfluidic channels. To meet this need, a simple push pin with a polydimethylsiloxane (PDMS) tip has been integrated into microfluidic networks to be placed within the microchannel to obstruct flow. This new valve design can attain on/off control of fluid flow without an external power source using readily-available, low-cost materials. The valve consists of a 14 gauge (1.6 mm) one inch piece of metal tubing with a PDMS pad at the tip to achieve a fluidic seal when pressed against a microfluidic channel's substrate. The metal tubing or pin is then either manually pushed down to block or pulled up to allow fluid flow. The valve was validated using a pressure transducer and fluorescent dye to determine the breakthrough pressure the valve can withstand over multiple cycles. In the first cycle, the median value for pressure withstood by the valve was 8.8 psi with a range of 17.5-2.7 psi. The pressure the valves were able to withstand during each successive trial was lower suggesting they may be most valuable as a method to control the initial introduction of fluids into a microfluidic device. These valves can achieve flow regulation within microfluidic devices, have a small dead volume, and are simple to fabricate and use, making this technique widely suitable for a range of applications.