Highly monodisperse sodium citrate-coated spherical silver nanoparticles (Ag NPs) with controlled sizes ranging from 10 to 200 nm have been synthesized by following a kinetically controlled seeded-growth approach via the reduction of silver nitrate by the combination of two chemical reducing agents: sodium citrate and tannic acid. The use of traces of tannic acid is fundamental in the synthesis of silver seeds, with an unprecedented (nanometric resolution) narrow size distribution that becomes even narrower, by size focusing, during the growth process. The homogeneous growth of Ag seeds is kinetically controlled by adjusting reaction parameters: concentrations of reducing agents, temperature, silver precursor to seed ratio, and pH. This method produces long-term stable aqueous colloidal dispersions of Ag NPs with narrow size distributions, relatively high concentrations (up to 6 × 1012 NPs/mL), and, more important, readily accessible surfaces. This was proved by studying the catalytic properties of as-synthesized Ag NPs using the reduction of Rhodamine B (RhB) by sodium borohydride as a model reaction system. As a result, we show the ability of citrate-stabilized Ag NPs to act as very efficient catalysts for the degradation of RhB while the coating with a polyvinylpyrrolidone (PVP) layer dramatically decreased the reaction rate.

Highly-monodisperse biocompatible and functionalizable sub-10 nm citrate-stabilized gold nanoparticles (Au NPs) have been synthesized following a kinetically controlled seeded-growth strategy. The use of traces of tannic acid together with an excess of sodium citrate during nucleation is fundamental in the formation of a high number (7•10 13 NP/mL) of small ~3.5 nm seeds with a very narrow distribution. A homogeneous nanometric growth of these seeds is then achieved by adjusting the reaction parameters: pH, temperature, sodium citrate concentration and gold precursor to seeds ratio. We use this method to produce Au NPs with a precise control over their sizes between 3.5 and 10 nm and a versatile surface chemistry allowing studying the size-dependent optical properties in this transition size regime lying between clusters and nanoparticles. Interestingly, an inflexion point is observed for NPs smaller than 8 nm in which the sensitivity of the Localized Surface Plasmon Resonance (LSPR) peak position as a function of NPs size and surface modifications dramatically increased. These studies are relevant in the design of the final selectivity, activity and compatibility of Au NPs, especially in those (bio)applications where size is a critical parameter (e.g. biodistribution, multiplex labeling and protein interaction).

Surface modifications of highly monodisperse citrate-stabilized gold nanoparticles (AuNPs) with sizes ranging from 3.5 to 150 nm after their exposure to cell culture media supplemented with fetal bovine serum were studied and characterized by the combined use of UV-vis spectroscopy, dynamic light scattering, and zeta potential measurements. In all the tested AuNPs, a dynamic process of protein adsorption was observed, evolving toward the formation of an irreversible hard protein coating known as Protein Corona. Interestingly, the thickness and density of this protein coating were strongly dependent on the particle size, making it possible to identify different transition regimes as the size of the particles increased: (i) NP-protein complexes (or incomplete corona), (ii) the formation of a near-single dense protein corona layer, and (iii) the formation of a multilayer corona. In addition, the different temporal patterns in the evolution of the protein coating came about more quickly for small particles than for the larger ones, further revealing the significant role that size plays in the kinetics of this process. Since the biological identity of the NPs is ultimately determined by the protein corona and different NP-biological interactions take place at different time scales, these results are relevant to biological and toxicological studies.