High aluminum loading incorporation in the SBA-15 silica structure was investigated. Different Si/Al molar ratios (15, 10, and 2) were evaluated. The SBA-15 and the aluminum-containing materials (Al-SBA-15) were prepared by the "pH adjusting" method with modifications. The mesoporous structure of the materials was demonstrated by the type IV isotherms. The SBA-15 pore changed from a cylindrical to a slit-like structure in the presence of higher aluminum content. X-ray diffraction (XRD) and highresolution transmission electron microscopy (HRTEM) pointed out that the structural order is compromised in the presence of a higher aluminum load in the Al-SBA-15 materials, although the mesoporous structure was preserved. Higher Al loading increases the total quantity of Lewis acid sites as well as generates Brönsted acid sites. CO adsorption FTIR spectroscopy suggests aluminum incorporation into the SBA-15 and generation of acid sites. The Si-O-Al linkage in the aluminum-containing materials was corroborated by UV-Vis DRS due to the presence of a peak centered at 216 nm related to the Al-O bond, which is ascribed to four-coordinated framework aluminum in the SBA-15 structure. XPS spectra of Al 2p suggested that the Al species are less oxidized than the Al2O3 phase giving some indication of Al incorporation into the SBA-15 framework. 27 Al MAS NMR results revealed that the aluminum species are in a tetrahedral oxygen coordination environment for Al-SBA-15 with Si/Al molar ratios of 15 and 10.Aluminum species in both tetrahedral and octahedral environments were evidenced for Al-SBA-15 with a Si/Al molar ratio of 2.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.