Three compounds bearing multiple adamantyl guest moieties and a fluorescent dye have been synthesized for the supramolecular patterning of beta-cyclodextrin (CD) host monolayers on silicon oxide using microcontact printing and dip-pen nanolithography. Patterns created on monolayers on glass were viewed by laser scanning confocal microscopy. Semi-quantitative analysis of the patterns showed that with microcontact printing approximately a single monolayer of guest molecules is transferred. Exposure to different rinsing procedures showed the stability of the patterns to be governed by specific supramolecular multivalent interactions. Patterns of the guest molecules created at CD monolayers were stable towards thorough rinsing with water, whereas similar patterns created on poly(ethylene glycol) (PEG) reference monolayers were instantly removed. The patterns on CD monolayers displayed long-term stability when stored under N(2), whereas patterns at PEG monolayers faded within a few weeks due to the diffusion of fluorescent molecules across the surface. Assemblies at CD monolayers could be mostly removed by rinsing with a concentrated CD solution, demonstrating the reversibility of the methodology. Patterns consisting of different guest molecules were produced by microcontact printing of one guest molecule and specific adsorption of a second guest molecule from solution to non-contacted areas, giving well-defined alternating assemblies. Fluorescent features of sub-micrometer dimensions were written using supramolecular dip-pen nanolithography.

The functionalization of optically transparent substrates is of importance, for example, in the field of biosensing. In this article, a new method for modification of silica surfaces is presented that is based on a photochemical reaction of terminal alkenes with the surface. This yields highly hydrophobic surfaces, which are thermally stable up to at least 400 degrees C. The formed monolayer provides chemical passivation of the underlying surface, according to studies showing successful blocking of platinum atomic layer deposition (ALD). The reaction is photochemically initiated, requiring light with a wavelength below 275 nm. X-ray photoelectron spectroscopy and infrared spectroscopy studies show that the alkenes initially bind to the surface hydroxyl groups in Markovnikov fashion. At prolonged reaction times (>5 h), however, oligomerization occurs, resulting in layer growth normal to the surface. The photochemical nature of the reaction enables the use of photolithography as a tool to constructively pattern silica surfaces. Atomic force microscopy shows that the features of the photomask are well transferred. The newly developed method can complement existing patterning methods on silica that are based on soft lithography.

No abstract

Porous anodic alumina (PAA) is a well-defined material that has found many applications. The range of applications toward sensing and recognition can be greatly expanded if the alumina surface is covalently modified with an organic monolayer. Here, we present a new method for the organic modification of PAA based on the reaction of terminal alkynes with the alumina surface. The reaction results in the the formation of a monolayer within several hours at 80 °C and is dependent on both oxygen and light. Characterization with X-ray photoelectron spectroscopy and infrared spectroscopy indicates formation of a well-defined monolayer in which the adsorbed species is an oxidation product of the 1-alkyne, namely, its α-hydroxy carboxylate. The obtained monolayers are fairly stable in water and at elevated temperatures, as was shown by monitoring the water contact angle. Modification with 1,15-hexadecadiyne resulted in a surface that has alkyne end groups available for further reaction, as was demonstrated by the subsequent reaction of N-(11-azido-3,6,9-trioxaundecyl)trifluoroacetamide with the modified surface. Biofunctionalization was explored by coupling 11-azidoundecyl lactoside to the surface and studying the subsequent adsorption of the lectin peanut agglutinin (PNA) and the yeast Candida albicans, respectively. Selective and reversible binding of PNA to the lactosylated surfaces was demonstrated. Moreover, PNA adsorption was higher on surfaces that exposed the β-lactoside than on those that displayed the α anomer, which was attributed to surface-associated steric hindrance. Likewise, the lactosylated surfaces showed increased colonization of C. albicans compared to unmodified surfaces, presumably due to interactions involving the cell wall β-glucan. Thus, this study provides a new modification method for PAA surfaces and shows that it can be used to induce selective adsorption of proteins and microorganisms.