DuqueJA, Fernandes SL, Bubola JP, Duarte MAH, Camilleri J, Marciano MA. The effect of mixing method on tricalcium silicate-based cement.International Endodontic Journal, 51, 69-78, 2018. Aim To evaluate the effect of three methods of mixing on the physical and chemical properties of tricalcium silicate-based cements. Methodology The materials evaluated were MTA Angelus and Portland cement with 20% zirconium oxide (PC-20-Zr). The cements were mixed using a 3 : 1 powder-to-liquid ratio. The mixing methods were manual (m), trituration (tr) and ultrasonic (us) activation. The materials were characterized by means of scanning electron microscope (SEM) and energy dispersive X-ray spectroscopy. Flowability was analysed according to ANSI/ADA 57/2012. Initial and final setting times were assessed following ASTM C266/08. Volume change was evaluated using a micro-CT volumetric method. Solubility was analysed according to ADA 57/2012. pH and calcium ion release were measured after 3, 24, 72 and 168 h. Statistical analysis was performed using two-way analysis of variance. The level of significance was set at P = 0.05. Results The SEM analysis revealed that ultrasonic activation was associated with a homogeneous distribution of particles. Flowability, volume change and initial setting time were not influenced by the mixing method (P > 0.05). Solubility was influenced by the mixing method (P < 0.05). For pH, at 168 h, significant differences were found between MTA-m and PC-20-Zr-m (P < 0.05). For calcium ion release, PC-20-Zr-tr had higher values than MTA-m at 3 h, and MTA-tr had higher values than PC-20-Zr-m at 168 h (P < 0.05). Conclusions The ultrasonic and trituration methods led to higher calcium ion release and pH compared with manual mixing for all cements, whilst the ultrasonic method produced smaller particles for the PC-20-Zr cement. Flow, setting times and volume change were not influenced by the mixing method used; however, it did have an impact on solubility.
Objective This study aimed to evaluate the influence of the NiTi wire in Conventional NiTi (ProTaper Universal PTU) and Controlled Memory NiTi (ProTaper Gold PTG) instrument systems on the quality of root canal preparation.Material and Methods Twelve mandibular molars with separate mesial canals were scanned using a high-definition microcomputed tomography system. The PTU and PTG instruments were used to shape twelve mesial canals each. The canals were scanned after preparation with F2 and F3 instruments of the PTU and PTG systems. The analyzed parameters included the remaining dentin thickness at the apical and cervical levels, root canal volume and untouched canal walls. Data was analyzed for statistical significance by the Friedman and Dunn’s tests. For the comparison of data between groups, the Mann-Whitney test was used.Results In the pre-operative analysis, there were no statistically significant differences between the groups in terms of the area and volume of root canals (P>.05). There was also no statistically significant difference between the systems with respect to root canal volume after use of the F2 and F3 instruments. There was no statistical difference in the dentin thickness at the first apical level between, before and after instrumentation for both systems. At the 3 cervical levels, the PTG maintained centralization of the preparation on the transition between the F2 and F3 instruments, which did not occur with the PTU. Conclusion The Conventional NiTi (PTU) and Controlled Memory NiTi (PTG) instruments displayed comparable capabilities for shaping the straight mesial root canals of mandibular molars, although the PTG was better than the PTU at maintaining the centralization of the shape in the cervical portion.
Objective:
The aim of this study was to evaluate the cyclic fatigue, torsional behavior and bending resistance of EdgeTaper Platinum [ETP (tip 25, taper 0.06)], Flex Gold [FG (tip 25, taper 0.08)], Pro-T [PT (tip 25, taper 0.08)] and ProTaper Gold [PTG (tip 25, taper 0.08)] systems.
Methods:
Rotary instruments of ETP, PT, FG, and PTG were used (n=30). Cyclic fatigue tests were performed using an artificial stainless-steel canal with a 60o angle and a 5-mm radius of curvature at body temperature (35°±1°C). The time and number of cycles to fracture (NCF) was recorded. The torsional test evaluated the torque and angle of rotation to failure at 3 mm from the tip according to ISO 3630-1. The fractured surface of each fragment was observed by using scanning electron microscopy (SEM). The bending test evaluated the torque required to bend the instruments at an angular deflection of 60°. Data were analyzed using one-way ANOVA and Tukey tests, and the level of significance was set at 5%.
Results:
The ETP had highest time until fracture and NCF than all the groups (P<0.05). The PTG had the highest torsional strength, followed by FG (P<0.05). The ETP had the highest angular rotation, followed by PT and PTG (P<0.05). The FG showed the highest bending resistance, followed by the PTG (P<0.05).
Conclusion:
In conclusion, the ETP and PT exhibited higher cyclic fatigue resistance, higher angular deflection values and lower bending force than FG and PTG. The PTG instruments showed the highest torsional strength and the lowest cyclic fatigue resistance.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.