Corrosion resistance properties of Ti/TiN and TiAl/TiAlN nanolayered multilayered coatings deposited on Ti6Al4V alloy substrates by unbalanced magnetron sputtering were investigated. The coatings contain a bi-layer thickness of Ti/TiN or TiAl/TiAlN ~3.5/4 nm and the total thickness of the coating is ~ 9 µm. Corrosion properties of the coatings were investigated using electrochemical impedance spectroscopy (EIS) for 30 days while immersed in 3.5 wt.% NaCl solution. EIS investigation of the coatings showed that the corrosion occurred due to the penetration of electrolyte and oxygen through the micro/nano pores present in the coatings. It was found that the TiAl/TIAlN coating offered corrosion protection superior to that of the Ti/TiN coating during the immersion study. Potentiodynamic polarization studies revealed that both coatings showed passive behaviour. Formation of a passive film on the coated surface during polarization enhanced the barrier properties of the coatings and provided anodic protection to the underlying alloy.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.