internal friction and the bulk modulus of silver were studied after irradiation a t 25 K with fast neutrons. The Frenkel defects produced by irradiation cause dislocation pinning and a consequent decrease in the Bordoni internal friction peak. With increasing irradiation dose the bulk modulus first increases, reaches a maximum and then decreases below its original value. The behaviour of the modulus with annealing up t o room temperature essentially corresponds to that of the residual electrical resistivity after low-temperatare neutron irradiation. A Frenkel defect concentration C F D gives rise to a relative dielastic modulus decrease AGjG which was determined to be AG/(G C F D ) = -33 f 9.Innere Reibung und Schubmodul von Silber wurden nach Bestrahlung bei 2 25 K mit schnellen Neutronen untersucht. Die durch die Bestrahlung erzeugten Frenkeldefekte bewirken Versetzungsverankerung und dadurch eine Verkleinerung des Bordoni-Maximums der Inneren Reibung und eine Erhiihung des Schubmoduls. Mit steigender Bestrahlungsdosis steigt der Schubmodul zuerst an, durchlauft ein Maximum und fallt dann wieder linter seinen Ausgangswert ab. Das Verhalten des Moduls hei der Erholung bis auf Raumtemperatur gleicht weitgehend dem des elektrischen Restwiderstandes nach Tieftemperaturbestrahlung init Neutronen. Eine Frenkeldefektkonzentration CFL) bewirkt eine relative dielastische Modulerniedrigung AG/G, fur die der Wert AG/(GcFD) = -33 $-9 ermittelt 1% nrde.

No abstract

No abstract

No abstract