The alkyl chain length of 1-alkyl-3-methylimidazolium bis(trifluoromethane sulfonyl)imide ([Rmim][(CF(3)SO(2))(2)N], R = methyl (m), ethyl (e), butyl (b), hexyl (C(6)), and octyl (C(8))) was varied to prepare a series of room-temperature ionic liquids (RTILs), and the thermal behavior, density, viscosity, self-diffusion coefficients of the cation and anion, and ionic conductivity were measured over a wide temperature range. The self-diffusion coefficient, viscosity, ionic conductivity, and molar conductivity change with temperature following the Vogel-Fulcher-Tamman equation, and the density shows a linear decrease. The pulsed-field-gradient spin-echo NMR method reveals a higher self-diffusion coefficient for the cation compared to that for the anion over a wide temperature range, even if the cationic radius is larger than that of the anion. The summation of the cationic and anionic diffusion coefficients for the RTILs follows the order [emim][(CF(3)SO(2))(2)N] > [mmim][(CF(3)SO(2))(2)N] > [bmim][(CF(3)SO(2))(2)N] > [C(6)mim][(CF(3)SO(2))(2)N] > [C(8)mim][(CF(3)SO(2))(2)N], which greatly contrasts to the viscosity data. The ratio of molar conductivity obtained from impedance measurements to that calculated by the ionic diffusivity using the Nernst-Einstein equation quantifies the active ions contributing to ionic conduction in the diffusion components, in other words, ionicity of the ionic liquids. The ratio decreases with increasing number of carbon atoms in the alkyl chain. Finally, a balance between the electrostatic and induction forces has been discussed in terms of the main contribution factor in determining the physicochemical properties.

Room-temperature ionic liquids (RTILs) based on 1-butyl-3-methylimidazolium ([bmim]) with a variety of fluorinated anions were prepared, and the thermal behavior, density, viscosity, self-diffusion coefficients of the cations and anions, and ionic conductivity were measured over a wide temperature range. The temperature dependencies of the self-diffusion coefficient, viscosity, ionic conductivity, and molar conductivity have been fitted to the Vogel-Fulcher-Tamman equation, and the best-fit parameters for the self-diffusion coefficient, viscosity, ionic conductivity, and molar conductivity have been estimated, together with the linear fitting parameters for the density. The self-diffusion coefficients determined for the individual ions by pulsed-fieldgradient spin-echo NMR method exhibit higher values for the cation compared with the anion over a wide temperature range, even if its radius is larger than that of the anionic radii. The summation of the cationic and anionic diffusion coefficients for the RTILs follows the order] at 30 °C, and the order of the diffusion coefficients greatly contrasts to the viscosity data. The ionic association is proposed from the results of the ratios of molar conductivity obtained from impedance measurements to that calculated by the ionic diffusivity using the Nernst-Einstein equation. The ratio for the ionic liquids follows the order30 °C and provides quantitative information on the active ions contributing to ionic conduction in the diffusion components.

A series of room-temperature ionic liquids (RTILs) were prepared with different cationic structures, 1-butyl-3-methylimidazolium ([bmim]), 1-butylpyridinium ([bpy]), N-butyl-N-methylpyrrolidinium, ([bmpro]), and N-butyl-N,N,N-trimethylammonium ([(n-C(4)H(9))(CH(3))(3)N]) combined with an anion, bis(trifluoromethane sulfonyl)imide ([(CF(3)SO(2))(2)N]), and the thermal property, density, self-diffusion coefficients of the cation and anion, viscosity, and ionic conductivity were measured over a wide temperature range. The self-diffusion coefficient, viscosity, ionic conductivity, and molar conductivity follow the Vogel-Fulcher-Tamman equation for temperature dependencies, and the best-fit parameters have been estimated, together with the linear fitting parameters for the density. The relative cationic and anionic self-diffusion coefficients for the RTILs, independently determined by the pulsed-field-gradient spin-echo NMR method, appear to be influenced by the shape of the cationic structure. A definite order of the summation of the cationic and anionic diffusion coefficients for the RTILs: [bmim][(CF(3)SO(2))(2)N] > [bpy][(CF(3)SO(2))(2)N] > [bmpro][(CF(3)SO(2))(2)N] > [(n-C(4)H(9))(CH(3))(3)N][(CF(3)SO(2))(2)N], has been observed, which coincides with the reverse order to the viscosity data. The ratio of molar conductivity obtained from the impedance measurements to that calculated by the ionic diffusivity using the Nernst-Einstein equation quantifies the active ions contributing to ionic conduction in the diffusion components and follows the order: [bmpro][(CF(3)SO(2))(2)N] > [(n-C(4)H(9))(CH(3))(3)N][(CF(3)SO(2))(2)N] > [bpy][(CF(3)SO(2))(2)N] > [bmim][(CF(3)SO(2))(2)N] at 30 degrees C.