AISI 347 austenitic steel is, as an example, used in nuclear energy piping systems. Piping filled with superheated steam or cooled water is particularly exposed to high stresses, whereupon local material properties in the pipes can change significantly, especially in the case of additional corrosive influences, leading to aging of the material. In the absence of appropriate information, such local material property variations are currently covered rather blanketly by safety factors set during the design of those components. An increase in qualified information could improve the assessment of the condition of such aged components. As part of the collaborative project “Microstructure-based assessment of the maximum service life of core materials and components subjected to corrosion and fatigue (MiBaLeB)”, the short-time procedure, StrainLife, was developed and validated by several fatigue tests. With this procedure, a complete S–N curve of a material can be determined on the basis of three fatigue tests only, which reduces the effort compared to a conventional approach significantly and is thus ideal for assessing the condition of aged material, where the material is often rare, and a cost-effective answer is often very needed. The procedure described is not just limited to traditional parameters, such as stress and strain, considered in destructive testing but rather extends into parameters derived from non-destructive testing, which may allow further insight into what may be happening within a material’s microstructure. To evaluate the non-destructive quantities measured within the StrainLife procedure and to correlate them with the aging process in a material, several fatigue tests were performed on unnotched and notched specimens under cyclic loading at room and elevated temperatures, as well as under various media conditions, such as distilled water and reactor pressure vessel boiling water (BWR) conditions.

The assessment of metallic materials used in power plants’ piping represents a big challenge due to the thermal transients and the environmental conditions to which they are exposed. At present, a lack of information related to degradation mechanisms in structures and materials is covered by safety factors in its design, and in some cases, the replacement of components is prescribed after a determined period of time without knowledge of the true degree of degradation. In the collaborative project “Microstructure-based assessment of maximum service life of nuclear materials and components exposed to corrosion and fatigue (MibaLeb)”, a methodology for the assessment of materials’ degradation is being developed, which combines the use of NDT techniques for materials characterization, an optimized fatigue lifetime analysis using short time evaluation procedures (STEPs) and numerical simulations. In this investigation, the AISI 347 (X6CrNiNb18-10) is being analyzed at different conditions in order to validate the methodology. Besides microstructural analysis, tensile and fatigue tests, all to characterize the material, a pressurized hot water pipe exposed to a series of flow conditions will be evaluated in terms of full-scale testing as well as prognostic evaluation, where the latter will be based on the materials’ data generated, which should prognose changes in the material’s condition, specifically in a pre-cracked stage. This paper provides an overview of the program, while the more material’s related aspects are presented in the subsequent paper.

No abstract