Core-shell type dual fluorescent nanoparticles (NPs) in the 16 nm diameter range with a selective ligand (cyclam) attached to the surface and two fluorophores--9,10-diphenyl-anthracene (donor, D) and pyrromethene PM 567 (acceptor, A)--embedded within the polymer core were synthesized and their fluorescent and copper-sensing properties were studied and compared to single D-doped and A-doped NPs. The acceptor (A) and donor (D) dyes were chosen to allow two sequential Förster resonance energy transfer (FRET) processes from D to A and from the encapsulated dyes to copper complexes that form at the surface and act as quenchers. NPs with different D/A loads were readily obtained by two consecutive entrapments of the dyes. Dual NPs present tunable fluorescence emission that is dependent on the doping ratio. FRET from D to A results in sensitized emission from A upon excitation of D, with FRET efficiencies reaching 80 % at high acceptor loads. A 9-fold amplification of the signal of A is observed at high D-to-A ratios. Single- and dual-dye-doped NPs were used to detect the presence of cupric ions in water by using the quenching of fluorescence as a transduction signal. In accordance with the spectral overlaps and the values of the critical distance (R0) of D- and A-copper complex pairs, the acceptor is much more sensitive than the donor. In dual fluorescent NPs, the sensitized emission of A is efficiently attenuated whereas the remaining emission of D is much less affected, allowing the detection of copper in a ratiometric manner upon excitation at a single (D) wavelength. Dual-dye-doped NPs with the highest acceptor loads (23 A-per-NP) were found to be the most sensitive for the detection of copper over a wide range of concentrations (20 nM to 8.5 microM). Owing to its great convenience and modularity, the cascade FRET strategy based on dual fluorescent NPs holds great promise for the design of various sensing nanodevices.

Stable translucent aqueous suspensions of azide‐functionalized cross‐linked nanoparticles (NPs), with diameters in the 15–20 nm range, were prepared using two synthetic approaches. Copolymerization of azidomethylstyrene (VBN3), styrene, and divinylbenzene in various oil‐in‐water microemulsions led to NPs with modulable azide contents (0.53–0.78 mmol/g) and surface over volume distributions. Surface modifications of reactive NPs bearing chlorobenzyl groups, produced by microemulsion copolymerization of vinylbenzylchloride, with sodium azide led to azido‐coated NPs with high densities of peripheral groups (0.13–0.45 mmol/g). It is shown that the nature of the surfactant used for the preparation of the microemulsion has an impact on the incorporation of VBN3 in the polymer particles as well as on the surface reaction yield. The azide‐functionalized NPs were used as clickable polymeric scaffolds for the grafting of sparingly water‐soluble dansyl and fluorescein derivatives through copper(I)‐catalyzed azide‐alkyne cycloaddition in water in the presence of surfactants as solubilizing agents to produce fluorescent NPs. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012