Type I collagen-PEO fibers and non-woven fiber networks were produced by the electrospinning of a weak acid solution of purified collagen at ambient temperature and pressure. As determined by high-resolution SEM and TEM. fiber morphology was influenced by solution viscosity, conductivity, and flow rate. Uniform fibers with a diameter range of 100-150 nm were produced from a 2-wt% solution of collagen-PEO at a flow rate of 100 microl min(-1). Ultimate tensile strength and elastic modulus of the resulting non-woven fabrics was dependent upon the chosen weight ratio of the collagen-PEO blend. 1H NMR dipolar magnetization transfer analysis suggested that the superior mechanical properties, observed for collagen-PEO blends of weight ratio 1:1, were due to the maximization of intermolecular interactions between the PEO and collagen components. The process outlined herein provides a convenient, non-toxic, non-denaturing approach for the generation collagen-containing nanofibers and non-woven fabrics that have potential application in wound healing, tissue engineering, and as hemostatic agents.

No abstract

The effectiveness of photomediated cross-linking of type I collagen gels in the presence of rat aortic smooth muscle cells (RASMC) as a method to enhance gel mechanical properties while retaining native collagen triple helical structure and maintaining high cell viability was investigated. Collagen was chemically modified to incorporate an acrylate moiety. Collagen methacrylamide was cast into gels in the presence of a photoinitiator along with RASMC. The gels were cross-linked using visible light irradiation. Neither acrylate modification nor the cross-linking reaction altered collagen triple helical content. The cross-linking reaction, however, moved the denaturation temperature beyond the physiologic range. A twelve-fold increase in shear modulus was observed after cross-linking. Cell viability in the range of 70% (n = 4, p > 0.05) was observed in the photo-cross-linked gels. Moreover the cells were able to contract the cross-linked gel in a manner commensurate with that observed for natural type I collagen. Methacrylate-mediated photo-cross-linking is a facile route to improve mechanical properties of collagen gels in the presence of cells while maintaining high cell viability. This enhances the potential for type I collagen gels to be used as scaffolds for tissue engineering.