Nowadays, there are many studies regarding with nanocomposite production including nano particles which aimed to gain many properties such as better strength, self-cleaning, and resistance to flammability into synthetic polymers. In nanocomposite production, the materials like clay, silica, metal oxides such as TiO2, Al2O3 are used. In present study, three different organically modified montmorillonite (MMT) clays of Cloisite 10A, 15A and 30B (3%) were added into polyethylene terephthalate (PET) polymer. Nanoclay and PET polymer were combined with melt blending method in terms of twin screw extruder. Internal and morphological properties of PET/clay nanocomposites were analyzed with scanning electron microscopy (SEM) images and XRD curves. And also, chemical and thermal properties of nanocomposite samples were studied. The findings and results of nanocomposites were compared with that of PET polymer. At the end of the study, the changes in PET polymer and the effect of clay type on material properties were determined.

Anahtar KelimelerKompleks koaservasyon, Kitosan, Polivinil alkol, Faz değiştiren madde Özet: Bu çalışmada, n-hekzadekan içeren mikrokapsüller fiziko kimyasal bir yöntem olan kompleks koaservasyon metoduyla üretilmiştir. Bu yöntemde, polikatyon ve polianyon polimerlerinin pH değişimine bağlı olarak kompleks oluşturması neticesinde çekirdek madde etrafında polimerce zengin bir duvar oluşumu gerçekleştirilmektedir. Bu yöntemde en önemli nokta pH'ın polimerlerin pozitif veya negatif yüklü olduğu değere ayarlanmasıdır. Bu şekilde oluşturulan kompleks mikrokapsül duvar yapısı daha sonra çapraz bağlayıcı madde ilavesi ile sağlamlaştırılmaktadır. Bu çalışmada mikrokapsüllerin duvar yapısını oluşturmak için polikatyon polimer olarak kitosan(CH), polianyon polimer olarak ise polivinil alkol ( Preparation and Characterization of N-hexadecane Microcapsules Chitosan-Poly(vinyl alcohol) Walled by Complex Coacervation Method KeywordsComplex coacervation, Chitosan, Polyvinyl alcohol, Phase change materials Abstract: In this study, microcapsules containing n-hexadecane were prepared using complex coacervation method which is a physicochemical method. In this method, polymer-rich wall formation around the core material is realized using the polycation and the polyanion polymers as a result of complex formation due to pH changes. The most important point in this method is the adjustment of pH to the value that polymers are positive or negative charged. Microcapsule complex wall structure formed is then stabilized by the addition of crosslinking agent. In this study, chitosan (CH) as polycation polymer and poly(vinyl alcohol) (PVA) as polyanion polymer were used to form microcapsules wall structure. In the study, surface active materials having different HLB value such as Span 20(8,6), Tween 20(16,7) Tween 40(15,6) and Tween 80(15,0), respectively were used as emulsifier. The wall material ratio of the microcapsules was determined as 0.5:1 while their wall/core ratio was chosen as 1:1.5. The particle size and size distribution by particle sizer (PSD), morphology by scanning electron microscopy (SEM), chemical structure by FT-IR spectroscopy, and heat storage and releasing properties of the prepared microcapsules by differential scanning calorimetry (DSC) were determined.

Özet: Çevrenin korunması bakımından atıkların geri kazanılması ve hammadde kaynağı olarak tekrar kullanılması için yöntemlerin geliştirilmesi büyük önem arz etmektedir. Bu çalışmada da, günlük yaşamda ve endüstriyel ürünlerde çok yaygın bir şekilde kullanılan polietilen tereftalat (PET) atıklarından kaynaklanan kirliliğin önlenmesi, plastik üretiminde atık haline dönüşen kısmın efektif bir şekilde değerlendirilebilmesi ile birlikte geri dönüşüm ve kompozit malzemelerin öneminden yola çıkarak nano boyutlu çeşitli partiküller içeren geri dönüşüm PET (rPET) esaslı nanokompozitlerin üretimi ve çeşitli özelliklerinin analizleri gerçekleştirilmiştir. Çalışmada, geri dönüşüm PET polimerleri ile nanopartiküller (bor, zeolit ve pomza) eriyikte birleştirme veya eriyikte harmanlama metodu kullanılarak çift vidalı ekstrüder içerisinde %3 oranında karıştırılmış ve granül halinde nanokompozitler elde edilmiştir. Çalışmada, partikül içerikli nanokompozitlerin polimer-partikül etkileşimi konusunda fikir sahibi olmak amacıyla bazı iç yapı ve termal özellikleri incelenmiştir. Bor, zeolit ve pomza içerikli nanokompozit üretimi konusunda ön bir araştırmanın gerçekleştirildiği çalışma sonucunda, kullanılan partikül türüne ve partikül dağılımına bağlı olarak farklı değişimlerin meydana geldiği belirlenmiştir.