Copper in steel causes metallurgical problems, but is pervasive in end-of-life scrap and cannot currently be removed commercially once in the melt. Contamination can be managed to an extent by globally trading scrap for use in tolerant applications and dilution with primary iron sources. However, the viability of long-term strategies can only be evaluated with a complete characterization of copper in the global steel system and this is presented in this paper. The copper concentration of flows along the 2008 steel supply chain is estimated from a survey of literature data and compared with estimates of the maximum concentration that can be tolerated in steel products. Estimates of final steel demand and scrap supply by sector are taken from a global stock-saturation model to determine when the amount of copper in the steel cycle will exceed that which can be tolerated. Best estimates show that quantities of copper arising from conventional scrap preparation can be managed in the global steel system until 2050 assuming perfectly coordinated trade and extensive dilution, but this strategy will become increasingly impractical. Technical and policy interventions along the supply chain are presented to close product loops before this global constraint.

No abstract

The supply of end-of-life steel scrap is growing, but residual copper reduces its value. Once copper attaches during hammer shredding, no commercial process beyond hand-picking exists to extract it, yet high-value flat products require less than 0.1 wt pct copper to avoid metallurgical problems. Various techniques for copper separation have been explored in laboratory trials, but as yet no attempt has been made to provide an integrated assessment of all options. Therefore, for the first time, a framework is proposed to define the full range of separation routes and evaluate their potential to remove copper, while estimating their energy and material input requirements. The thermodynamic, kinetic, and technological constraints of the various techniques are analyzed to show that copper could be removed to below 0.1 wt pct with relatively low energy and material consumption. Higher-density shredding allows for greater physical separation, but requires proper incentivization. Vacuum distillation could be viable with a reactor that minimizes radiation heat losses. High-temperature solid scrap pre-treatments would be less energy intensive than melt treatments, but their efficacy with typical shredded scrap is yet unconfirmed. The framework developed here can be applied to other impurity-base metal systems to coordinate process innovation as the scrap supply expands.

No abstract

Copper contamination of end-of-life steel scrap is the main barrier to high-quality recycling. Preferential melting of copper from solid steel scrap is a potential extraction technique, which could be integrated into conventional scrap re-melting with little additional energy. However, previous investigations show removal of liquid copper is limited by its adherence to solid scrap. Preventing wetting between liquid copper and steel is essential to enable separation. The carbon content of steel, initial surface oxidation, and applied coatings effect wetting behavior, but have not been systematically studied. In this study, the individual and combined effects of these parameters on wetting behavior in an inert gaseous environment are observed with a heating microscope. Carbon content appears to be the most significant factor: blistering of the oxide scale on medium-carbon steels causes liquid copper to flow rapidly between the oxide and steel substrate. Liquid copper exhibited a stable droplet on low-carbon steel, regardless of the initial level of oxidation. The tested coatings did not consistently improve nonwetting behavior, but impaired the connection between the scale and steel substrate. This study confirms the potential of the preferential melting technique, but further investigation is needed to determine the most robust process conditions to handle diverse, fragmented scrap at an industrial scale.