The fabrication processes of p-type regions for vertical GaN power devices are investigated. A p-type body layer in a trench gate metal-oxide-semiconductor field-effect transistor requires precise control of the effective acceptor concentration, which is equal to the difference between the Mg acceptor concentration (Na) and the compensating donor concentration (Nd). The carbon atoms incorporated during growth via metalorganic vapor phase epitaxy substitute nitrogen sites (CN) and function as donor sources in a p-type GaN layer. Since interstitial H atoms (Hi) also compensate holes, their removal from an Mg-doped layer is crucial. Extended anneals to release H atoms cause the formation of extra hole traps. The p+ capping layer allows effective and rapid removal of H atoms from a p-type body layer owing to the electric field across the p+/p– junction. On the other hand, selective area p-type doping via Mg ion implantation is needed to control the electrical field distribution at the device edge. Ultrahigh-pressure annealing (UHPA) under a nitrogen pressure of 1 GPa enables post-implantation annealing up to 1753 K without thermal decomposition. Cathodoluminescence spectra and Hall-effect measurements suggest that the acceptor activation ratio improves dramatically by annealing above 1673 K as compared to annealing at up to 1573 K. High-temperature UHPA also induces Mg atom diffusion. We demonstrate that vacancy diffusion and the introduction of H atoms from the UHPA ambient play a key role in the redistribution of Mg atoms.
Magnesium ion implantation has been performed on a GaN
substrate, whose surface has a high thermal stability, thus allowing postimplantation annealing without the use of a protective layer. The current–voltage characteristics of p–n diodes fabricated on GaN
showed distinct rectification at a turn-on voltage of about 3 V, although the leakage current varied widely among the diodes. Coimplantation with magnesium and hydrogen ions effectively suppressed the leakage currents and device-to-device variations. In addition, an electroluminescence band was observed at wavelengths shorter than 450 nm for these diodes. These results provide strong evidence that implanted magnesium ions create acceptors in GaN
.
Sources of carrier compensation in n-type and p-type GaN layers grown by metalorganic vapor phase epitaxy were quantitatively identified by a combination of Hall-effect analysis and deep level transient spectroscopy. For n-type GaN, we identified three electron compensation sources: residual carbon atoms likely sitting on nitrogen sites (CN), an electron trap at the energy level of EC –0.6 eV (the E3 trap), and self-compensation appearing with increasing donor concentration. We showed that the CN also play a key role in hole compensation in p-type GaN by forming donor-like charged states. We also investigated the reduction of acceptor concentrations (Na) in highly Mg-doped GaN. Atomic-resolution scanning transmission electron microscopy revealed that electrically inactive Mg atoms of 3/2 atomic layers are segregated at the boundary of pyramidal inversion domains. The Na reduction can be explained by this Mg segregation.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.