We detail the formation and properties associated with stable glasses (SG) formed by a series of structural analogues of 1,3-bis(1-naphthyl)-5-(2-naphthyl)benzene (α,α,β-TNB), a well-studied SG former. Five compounds with similar structural properties were synthesized and physical vapor-deposited with a constant deposition rate at various substrate temperatures (Tdep) in the range between 0.73 Tg and 0.96 Tg. These molecules include α,α,β-TNB, 3,5-di(naphthalen-1-yl)-1-phenylbenzene (α,α-P), 9-(3,5-di(naphthalen-1-yl)phenyl)anthracene (α,α-A), 9,9'-(5-(naphthalen-2-yl)-1,3-phenylene)dianthracene (β-AA), and 3,3',5,5'-tetra(naphthalen-1-yl)-1,1'-biphenyl (α,α,α,α-TNBP). Ellipsometry was used to study the transformations from the as-deposited glasses into ordinary glasses (OG). The stability of each film was evaluated by measuring the fictive temperature (Tf) and density difference between the as-deposited glass and OG. It is demonstrated that all five molecules can form SGs upon vapor deposition in this temperature range. In-depth studies on the dependence of the stability of as-deposited glasses upon Tdep were performed with three molecules, α,α,β-TNB, α,α-P, and α,α-A. The general trends of stability were comparable at the same Tdep/Tg for these three compounds. Similar to previous studies on α,α,β-TNB, vapor-deposited glasses of α,α-P and α,α-A formed the most stable structures around Tdep = 0.8-0.85 Tg. The most stable glass of each molecule showed the lowest thermal expansion coefficient compared to OG and a positive optical birefringence. However, the SGs of α,α-A were less stable compared to α,α-P and α,α,β-TNB at the relative Tdep/Tg. Based on Arrhenius extrapolation of the aging time, as a measure of stability, the most stable α,α-A glass was only aged for a few years as opposed to hundreds or thousands of years for other glasses. We hypothesize that the reduced stability is due to slower mobility at the free surface of α,α-A glass compared to the other two molecules.

Birefringence in stable glasses produced by physical vapor deposition often implies molecular alignment similar to liquid crystals. As such, it remains unclear whether these glasses share the same energy landscape as liquid-quenched glasses that have been aged for millions of years. Here, we produce stable glasses of 9-(3,5-di(naphthalen-1-yl)phenyl)anthracene molecules that retain three-dimensional shapes and do not preferentially align in a specific direction. Using a combination of angle- and polarization-dependent photoluminescence and ellipsometry experiments, we show that these stable glasses possess a predominantly isotropic molecular orientation while being optically birefringent. The intrinsic birefringence strongly correlates with increased density, showing that molecular ordering is not required to produce stable glasses or optical birefringence, and provides important insights into the process of stable glass formation via surface-mediated equilibration. To our knowledge, such novel amorphous packing has never been reported in the past.

Nitrile-substituted cyclopropanes are readily synthesized in a stereocontrolled fashion from the intermolecular cyclopropanation between 2-diazo-2-phenylacetonitrile and electron-rich olefins, catalyzed by the chiral dirhodium complex, Rh(2)(S-PTAD)(4).

A mild palladium catalyzed coupling of reactive aldehyde homoenolates with aryl bromides is described. Aldehyde homoenolates are generated by ring opening of cyclopropanols via a C-C cleavage step. The coupling generates aldehyde products at room temperature in 59-93% yield.

We report the synthesis and characterization of an analogous series of small organic molecules derived from a well-known glass former, 1,3-bis(1-naphthyl)-5-(2-naphthyl)benzene (α,α,β-TNB). Synthesized molecules include α,α,β-TNB, 3,5-di(naphthalen-1-yl)-1-phenylbenzene (α,α-P), 9-(3,5-di(naphthalen-1-yl)phenyl)anthracene (α,α-A), 9,9'-(5-(naphthalen-2-yl)-1,3-phenylene)dianthracene (β-AA) and 3,3',5,5'-tetra(naphthalen-1-yl)-1,1'-biphenyl (α,α,α,α-TNBP). The design of molecules was based on increasing molecular weight with varied π-π interactions in one or more substituents. The synthesis is based on Suzuki cross-coupling of 1-bromo-3-chloro-5-iodobenzene with arylboronic acids, which allows attachment of various substituents to tailor the chemical structure. The bulk compounds were characterized using NMR spectroscopy and differential scanning calorimetry (DSC). Thin films of these compounds were produced using physical vapor deposition and were subsequently annealed above the glass transition temperatures (Tg). For each molecular glass, cooling rate-dependent glass transition temperature measurements (CR-Tg) were performed using ellipsometry as a high-throughput method to characterize thin film properties. CR-Tg allows rapid characterization of glassy properties, such as Tg, apparent thermal expansion coefficients, apparent activation energy at Tg and fragility. DSC measurements confirmed the general trend that increasing molecular weight leads to increasing melting point (Tm) and Tg. Furthermore, CR-Tg provided evidence that the introduction of stronger π-interacting substituents in the chosen set of structural analogues increases fragility and decreases the ability to form glasses, such that β-AA has the largest fragility and highest tendency to crystallize among all the compounds. These strong interactions also significantly elevate Tg and promote more harmonic intermolecular potentials, as observed by decreasing value of the apparent thermal expansion coefficient.