Ordered arrays of copper nanostructures were fabricated and modified with porphyrin molecules in order to evaluate fluorescence enhancement due to the localized surface plasmon resonance. The nanostructures were prepared by thermally depositing copper on the upper hemispheres of two-dimensional silica colloidal crystals. The wavelength at which the surface plasmon resonance of the nanostructures was generated was tuned to a longer wavelength than the interband transition region of copper (>590 nm) by controlling the diameter of the underlying silica particles. Immobilization of porphyrin monolayers onto the nanostructures was achieved via self-assembly of 16-mercaptohexadecanoic acid, which also suppressed the oxidation of the copper surface. The maximum fluorescence enhancement of porphyrin by a factor of 89.2 was achieved as compared with that on a planar Cu plate (CuP) due to the generation of the surface plasmon resonance. Furthermore, it was found that while the fluorescence from the porphyrin was quenched within the interband transition region, it was efficiently enhanced at longer wavelengths. It was demonstrated that the enhancement induced by the proximity of the fluorophore to the nanostructures was enough to overcome the highly efficient quenching effects of the metal. From these results, it is speculated that the surface plasmon resonance of copper has tremendous potential for practical use as high functional plasmonic sensor and devices.

We demonstrate that Pd nanospheres exhibit much higher susceptibility of the localized surface plasmon resonance (LSPR) peak to medium refractive index changes than commonly used plasmonic sensing materials such as Au and Ag. The susceptibility of spherical Au nanoparticle-core/Pd-shell nanospheres (Au/PdNSs, ca. 73 nm in diameter) was found to be 4.9 and 2.5 times higher, respectively, than those of Au (AuNSs) and Ag nanospheres (AgNSs) having similar diameters. The experimental finding was theoretically substantiated using the Mie exact solution. We also showed from a quasi-static (QS) approximation framework that the high susceptibility of Pd LSPR originates from the smaller dispersion of the real part of its dielectric function than those of Au and Ag LSPR around the resonant wavelength. We conclude that the Pd nanoparticle is a promising candidate of "the third plasmonic sensing material" following Au and Ag to be used in ultrahigh-sensitive LSPR sensors.

The effect of localized electric fields on the photocurrent responses of phthalocyanine that was self-assembled on a gold nanoparticle film was investigated by comparing the conventional and the total internal reflection (TIR) experimental systems. In the case of photocurrent measurements, self-assembled monolayers (SAMs) of a thiol derivative of palladium phthalocyanine (PdPc) were prepared on the surface of gold-nanoparticle film that was fixed on the surface of indium-tin-oxide (ITO) substrate via a polyion (PdPc/AuP/polyion/ITO) or on the ITO surface (PdPc/ITO). Photocurrent action spectra from the two samples were compared by using the conventional spectrometer, and were found that PdPc/AuP/polyion/ITO gave considerably larger photocurrent signals than PdPc/ITO under the identical concentration of PdPc. In the case of the TIR experiments for the PdPc/AuP/polyion/ITO and the PdPc/AuP/Glass systems, incident-angle profiles of photocurrent and emission signals were correlated with each other, and they were different from that of the PdPc/ITO system. Accordingly, it was demonstrated that the photocurrent signals were certainly enhanced by the localized electric fields of the gold-nanoparticle film.

A self-assembled monolayer of porphyrins fabricated on the surface of an electrochemically deposited gold nanostructure exhibits enormous enhancement of photocurrent due to porphyrin excitation, especially in the near-infrared region, where localized surface plasmon resonance was responsible.