Extensive durability problems such as weathering and degradation are found in historic Scandinavian brick masonry buildings, especially from the neo-Gothic period. These are largely due to the crystallization of salts and frost action in the bricks and mortars. This article aims to show and illustrate which salts and crystals are found in historic brick masonry buildings and to describe their appearance and behavior. An additional aim is to explore possibilities of preventing salt-related damage on internal masonry wall surfaces, such as using hemp-lime sacrificial plaster beneath the plaster. The objective is to show the mechanisms behind salt-related problems and to perform a case study and a laboratory study on salt-damaged brick masonry containing sodium sulphate. In order to prevent and stop damage to the masonry, it is important to be able to identify the nature of the salt damage and the type of salt that caused the damage. Neo-Gothic brick masonry buildings require well-planned, continuous maintenance of the masonry. It is therefore of the utmost importance to have an understanding of the complex functions of the masonry and of the salts that can cause damage to these historic buildings.

With an increased focus on reducing greenhouse gas emissions, energy saving is of great importance in all sectors of society. EU directives set targets for member states to reduce energy use in buildings. Energy saving in historic buildings requires special measures, balancing energy-saving renovations against the preservation of heritage values. Traditional constructions are open to vapor diffusion and generally work differently from modern constructions. Modern materials in traditional constructions sometimes damages the original material as they are usually diffusion-tight. The aim of this study was to investigate whether hemp-lime could be used as an insulation material to improve the energy efficiency of historic timber building envelopes with a rendered façade in Sweden. The objective was to determine the actual energy savings for space heating. An additional objective was to determine the actual thermal transmittance and to study thermal buffering through in-situ measurements in a full-scale wall renovated with hemp-lime. Two full-scale wall sections were constructed at the Energy and Building Design laboratory at Lund University: A traditional post-and-plank wall with a lime render (80 mm), and a post-and-plank wall with a hemp-lime render (90 mm). Energy use for space heating was monitored continuously over a period of one year. The wall with a hemp-lime render required 33% less energy for space heating than the traditional post-and-plank wall with a lime render. This was accomplished without changing the framework, appearance or material in the render and without drastically changing the hygric properties of the façade. From the gathered data, the thermal transmittance (U-values) for both walls was calculated using two different methods, one based on material properties and the other based on energy use data. For both walls, thermal transmittance based on actual energy use data during the heating period was lower than what was expected from their material properties. This indicates that more material properties than thermal conductivity and material thickness need to be taken into account when performing energy use calculations. With hemp-lime, a renovation can be accomplished without damaging the timber structure and wooden slats, and it can be done with local traditional materials and building methods with no difference in appearance to a traditional lime render. This allows for heritage values to be preserved, while also allowing the building to comply with modern standards and with increased thermal comfort and reduced energy use.

No abstract

Microbial growth often thrives in humid conditions, at high relative humidity. Moulds are complex organisms; many types of mould are able to survive strong variations in humidity and temperature, such as those on building façades. For some building materials a critical relative humidity is determined, which functions as a theoretical threshold; at this (or lower) relative humidity microbial growth will likely not occur. Hemp-lime is a building material that consists of hemp shiv (the woody core parts of the hemp stem) and building lime. It is a material that can be used for walls, and even though it has been used for more than 20 years, thusfar little is known about its critical moisture levels for microbial growth. The aim of this research was therefore to determine at what relative humidity microbial growth occurs on carbonated hemp-lime material, and to study if there is a protective influence of a carbonated lime binder on the hemp shiv. The objective was to study microbial growth on hemp shiv, hemp-lime and on hemp with a thin layer of lime at three relative humidity (75 %, 85 % and 95 %) and at two different temperatures (15°C and 23°C); conditions that could occur naturally in a hemp-lime façade exposed to high rain loads in a northern European climate. Hemp shiv seems to have a relatively low resistance to microbial growth, similar to that of wood. However, because the hemp is protected by lime it can withstand much higher relative humidity without microbial growth occurring on the material. The critical moisture level for hemp-lime seemed to occur between 75 and 85 % RH, while the material was completely without microbial growth at 75 % RH. The lime had a protective effect on the hemp and acted as a mould inhibitor, both over time and with varying temperature and humidity.

No abstract