In the present study, we have investigated the effect of post-welding heat treatment (PWHT) of quenching and tempering (QT) on the microstructure and mechanical properties of welded boron steel joints processed using laser-arc hybrid welding on two commercial filler materials, SM80 (Type-I) and ZH120 (Type-II). The microstructure and mechanical properties of the weld joints were characterized via optical microscopy, Vickers microhardness, and the uniaxial tensile test. The macrostructure of the weld joint was composed of a fusion zone (FZ), heat-affected zone (HAZ), and base metal zone (BMZ). After the QT-PWHT, the QT specimens revealed the V-shape hardness distribution across the weld joint, while the as-welded specimen exhibited the M-shape hardness distribution. As a result, the QT specimens revealed the premature fracture with little reduction in the area at the interface between the HAZ and FZ, while the as-welded specimen exhibited the local necking and rupture in the BMZ. In addition, the Type-II filler material with a greater value of equivalent carbon content was rarely influenced by the tempering, maintaining its hardness in the as-quenched status, while the Type-I filler material showed a gradual decrease in hardness with the tempering time. The results demonstrate that the Type-II weld joint outperformed the Type-I weld joint in terms of the structural integrity of welded parts.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.