Background: The leaves of Perilla frutescens, commonly called perilla and used for food in Korea, contain components with a variety of biological effects and potential therapeutic applications. The purpose of this study was to identify the components of 70% ethanol extracted Perilla frutescens (EEPF) and determine its inhibitory effects on oral microbial activity and production of nitric oxide (NO) and prostaglandin E2 (PGE2) in lipopolysaccharides (LPS)-stimulated Raw264.7 macrophages, consequently, to confirm the possibility of using EEPF as a functional component for improving the oral environment and preventing inflammation. Methods: One kg of P. frutescens leaves was extracted with 70% ethanol and dried at −70 o C. EEPF was analyzed using high-performance liquid chromatography analysis, and antimicrobial activity against oral microorganisms was revealed using the disk diffusion test. Cell viability was elucidated using a methylthiazolydiphenyl-tetrazolium bromide assay, and the effect of EEPF on LPS-induced morphological variation was confirmed through microscopic observation. The effect of EEPF on LPS-induced production of pro-inflammatory mediators, NO and PGE2 was confirmed by the NO assay and PGE2 enzyme-linked immunosorbent assay. Results: The main component of EEPF was rosemarinic acid, and EEPF showed weak anti-bacterial and anti-fungal effects against microorganisms living in the oral cavity. EEPF did not show toxicity to Raw264.7 macrophages and had inhibitory effects on the morphological variations and production of pro-inflammatory mediators, NO and PGE2 in LPS-stimulated Raw264.7 macrophages. Conclusion: EEPF can be used as a functional material for improving the oral environment through the control of oral microorganisms and for modulating inflammation by inhibiting the production of inflammatory mediators.

No abstract

Background: The purpose of this study was to investigate the effects of commercially available calamansi soju and other alcoholic beverages on the microhardness and erosion of resin restorations. Methods: In this study, we evaluated the effects of Calamansi soju, Chamisul fresh, Cass fresh, and Gancia Moscato D'asti on resin restorations. Jeju Samdasoo and Coca-Cola were used as negative and positive controls, respectively. Specimens to be immersed in the beverages were manufactured using composite resin according to the product instructions. In each group, the surface microhardness was measured using a surface microhardness instrument before and after immersion for 5, 15, 30, and 60 minutes. The pattern of change in the surface of the composite resin was observed under a scanning electron microscope (SEM). Paired t-tests, one-way ANOVA, and repeated measures ANOVA were performed to compare the surface microhardness of the specimens, and the Tukey test was used as a post hoc test. Results: The pH of all beverages except Jeju Samdasoo was ＜5.5, which is the critical pH that can induce erosion. The difference in surface microhardness of the composite resin before and after immersion for 60 minutes was significant in all groups. In particular, the largest change in surface microhardness was observed in the calamansi soju group. In the SEM analysis, loss of composite resin was observed in all groups except the Jeju Samdasoo group, and rough surfaces with pores of various sizes were observed. Conclusion: In this study, all beverages except Jeju Samdasoo decreased the microhardness of the composite resin surface, and it was confirmed that calamansi soju had the greatest change.