This study investigated actively brazing Alumina-to-Alumina with Ag-Cu-Ti as the filler metal system and Alumina-to-Copper with Cu-Ti-Co as the filler-metal system. The research was conducted on four samples, two of which were alumina brazed to alumina (Samples 1 & 2), and the other two were alumina brazed to copper (Samples 3 & 4). The filler metal composition for each sample was as follows: Sample 1 consisted of Cu-96%, and Ti-4%; Sample 2 consisted of Ag-70%, Cu-26%, and Ti-4%; Sample 3 consisted of Cu-85%, Ti-10%, and Co-5%; and Sample 4 consisted of Cu-55%, Ti-40%, and Co-5%. The phase transformations between the filler and base metal of each brazed joint were studied using EDS, SEM, optical microscopy, and X-ray diffraction.