This study shows the energy optimization and stabilization in the time of solutions composed of H2O + TX-100 + Multi-Wall Carbon Nanotubes (MWCNTs), used to improve the mechanical properties of Portland cement pastes. For developing this research, sonication energies at 90, 190, 290, 340, 390, 440, 490 and 590 J/g are applied to a colloidal substance (MWCNTs/TX-100 + H2O) with a molarity of 10 mM. Raman spectroscopy analyses showed that, for energies greater than 440 J/g, there are ruptures and fragmentation of the MWCNTs; meanwhile at energies below 390 J/g, better dispersions are obtained. The stability of the dispersion over time was evaluated over 13 weeks using UV-vis spectroscopy and Zeta Potential. With the most relevant data collected, sonication energies of 190, 390 and 490 J/g, at 10 mM were selected at the first and the fourth week of storage to obtain Portland cement specimens. Finally, we found an improvement of the mechanical properties of the samples built with Portland cement and solutions stored for one and four weeks; it can be concluded that the MWCNTs improved the hydration period.

Silver nanoparticles (AgNPs) have aroused great interest for applications as fungicides in agriculture. This study reports the synthesis of AgNPs by green chemistry using silver nitrate (AgNO3) as the precursor agent and a coriander leaf extract as the reducing agent and surfactant. The evaluation of their antifungal properties was carried out when placed in contact with Fusarium solani and Rhizopus stolonifer phytopathogens. The extract and AgNP characterizations were performed using UV–Vis spectroscopy, X-ray diffraction (XRD), Fourier Transform Infrared Spectroscopy (FTIR), dynamic light scattering (DLS) and scanning electron microscopy (SEM). The evaluation of antifungal properties was carried out by exposing the phytopathogens to different concentrations of AgNPs in PDA (Potato Dextrose Agar). It was found that it was possible to identify the presence of flavones and flavonoids in the extract, compounds that were also involved in the synthesis process of AgNPs. In addition, the UV–Vis analysis of the obtained AgNPs by green chemistry showed resonance peaks at around 428 nm. Furthermore, a high distribution of AgNP sizes, with high concentrations of below 100 nm, was identified, according to DLS measurements. Using SEM images, the information provided by DLS was confirmed, and a crystallite size of 29.24 nm was determined with the help of XRD measurements. Finally, when exposing the phytopathogens to the action of AgNPs, it was concluded that, at a concentration of 1 mg/mL AgNPs, their growth was totally inhibited.