No abstract

No abstract

It is a huge challenge to achieve highly efficient fire retardance with no mechanical damage to polymers. In our current research, a novel core-shell titanium dioxide@diphenylphosphinic (TiO@DPP) nanosphere was first synthesized through a hydrothermal reacting process, and applied in simultaneously enhancing the fire retardance and mechanical properties of polycarbonate (PC). The well-designed TiO@DPP exhibited a significant effect on combustion performance and mechanical reinforcement of PC. At only 0.10 wt % of TiO@DPP, PC/TiO@DPP passed the UL-94 V-0 rating, and its oxygen index value rose to 29.3%. Moreover, the peak value of the heat release rate was remarkably decreased by 34.1% in the combustion test, accompanied by the formation of more compacted char layer and the release of more incombustible gas. Equally important another aspect is that the PC containing only 0.10 wt % of TiO@DPP possessed higher elongation at break and higher tensile strength than pure PC, correspondingly increased by 27.7 and 14.7%. The analysis of the flame-retardant mechanism revealed that the improved fire retardance of PC is primarily ascribed to the barrier action of a cross-linking network containing phosphorus and titanium, the dilution of nonflammable gases such as HO, and the quenching effect of free radicals which are from the phosphorous group in the gas phase. All these experimental results demonstrate that the core-shell hybrid TiO@DPP may achieve a simultaneous significant improvement in fire retardance and mechanical properties of PC.

Natural rubber (NR) as a kind of commercial polymer or engineering elastomer is widely used in tires, dampers, suspension elements, etc., because of its unique overall performance. For some NR products, their work environment is extremely harsh, facing a serious fire safety challenge. Accordingly, it is important and necessary to endow NR with flame retardancy via different strategies. Until now, different methods have been used to improve the flame retardancy of NR, mainly including intrinsic flame retardation through the incorporation of some flame-retarding units into polymer chains and additive-type flame retardation via adding some halogen or halogen-free flame retardants into NR matrix. For them, the synergistic flame-retarding action is usually applied to simultaneously enhance flame retardancy and mechanical properties, in which some synergistic flame retardants such as organo-montmorillonite (OMMT), carbon materials, halloysite nanotube (HNT), etc., are utilized to achieve the above-mentioned aim. The used flame-retarding units in polymer chains for intrinsic flame retardation mainly include phosphorus-containing small molecules, an unsaturated chemical bonds-containing structure, a cross-linking structure, etc.; flame retardants in additive-type flame retardation contain organic and inorganic flame retardants, such as magnesium hydroxide, aluminum hydroxide, ammonium polyphosphate, and so on. Concerning the flame retardation of NR, great progress has been made in the past work. To achieve the comprehensive understanding for the strategy and recent progress in the flame retardation of NR, we thoroughly analyze and discuss the past and current flame-retardant strategies and the obtained progress in the flame-retarding NR field in this review, and a brief prospect for the flame retardation of NR is also presented.

No abstract