The MnO(x) and CeO(x) were in situ supported on carbon nanotubes (CNTs) by a poly(sodium 4-styrenesulfonate) assisted reflux route for the low-temperature selective catalytic reduction (SCR) of NO with NH(3). X-Ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution TEM (HRTEM), X-ray photoelectron spectroscopy (XPS), H(2) temperature-programmed reduction (H(2)-TPR) and NH(3) temperature-programmed desorption (NH(3)-TPD) have been used to elucidate the structure and surface properties of the obtained catalysts. It was found that the in situ prepared catalyst exhibited the highest activity and the most extensive operating-temperature window, compared to the catalysts prepared by impregnation or mechanically mixed methods. The XRD and TEM results indicated that the manganese oxide and cerium oxide species had a good dispersion on the CNT surface. The XPS results demonstrated that the higher atomic concentration of Mn existed on the surface of CNTs and the more chemisorbed oxygen species exist. The H(2)-TPR results suggested that there was a strong interaction between the manganese oxide and cerium oxide on the surface of CNTs. The NH(3)-TPD results demonstrated that the catalysts presented a larger acid amount and stronger acid strength. In addition, the obtained catalysts exhibited much higher SO(2)-tolerance and improved the water-resistance as compared to that prepared by impregnation or mechanically mixed methods.

No abstract

Nanoflaky MnO(x) on carbon nanotubes (nf-MnO(x)@CNTs) was in situ synthesized by a facile chemical bath deposition route for low-temperature selective catalytic reduction (SCR) of NO with NH₃. This catalyst was mainly characterized by the techniques of X-ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscopy (SEM), N₂ adsorption-desorption analysis, X-ray photoelectron spectroscopy (XPS), H₂ temperature-programmed reduction (H₂-TPR) and NH₃ temperature-programmed desorption (NH₃-TPD). The SEM, TEM, XRD results and N₂ adsorption-desorption analysis indicated that the CNTs were surrounded by nanoflaky MnO(x) and the obtained catalyst exhibited a large surface area as well. Compared with the MnO(x)/CNT and MnO(x)/TiO₂ catalysts prepared by an impregnation method, the nf-MnO(x)@CNTs presented better NH₃-SCR activity at low temperature and a more extensive operating temperature window. The XPS results showed that a higher atomic concentration of Mn(4+) and more chemisorbed oxygen species existed on the surface of CNTs for nf-MnO(x)@CNTs. The H₂-TPR and NH₃-TPD results demonstrated that the nf-MnO(x)@CNTs possessed stronger reducing ability, more acid sites and stronger acid strength than the other two catalysts. Based on the above mentioned favourable properties, the nf-MnO(x)@CNT catalyst has an excellent performance in the low-temperature SCR of NO to N₂ with NH₃. In addition, the nf-MnO(x)@CNT catalyst also presented favourable stability and H₂O resistance.