In this study, the impact of steel fibres and Silica Fume (SF) on the mechanical properties of recycled aggregate concretes made of two different types of Recycled Coarse Aggregates (RCA) sourced from both low- and high-strength concretes were evaluated through conducting 60 compressive strength tests. The RCAs were used as replacement levels of 50% and 100% of Natural Coarse Aggregates (NCA). Hook-end steel fibres and SF were also used in the mixtures at the optimised replacement levels of 1% and 8%, respectively. The results showed that the addition of both types of RCA adversely affected the compressive strength of concrete. However, the incorporation of SF led to compressive strength development in both types of concretes. The most significant improvement in terms of comparable concrete strength and peak strain with ordinary concrete at 28 days was observed in the case of using a combination of steel fibres and SF in both recycled aggregate concretes, especially with RCA sourced from high strength concrete. Although using SF slightly increased the elastic modulus of both recycled aggregate concretes, a substantial improvement in strength was observed due to the reinforcement with steel fibre and the coexistence of steel fibre and SF. Moreover, existing models to predict the elastic modulus of both non-fibrous and fibrous concretes are found to underestimate the elastic modulus values. The incorporation of SF changed the compressive stress-strain curves for both types of RCA. The addition of steel fibre and SF remarkably improved the post-peak ductility of recycled aggregates concretes of both types, with the most significant improvement observed in the case of RCA sourced from a low-strength parent concrete. The existing model to estimate the compressive stress-strain curve for steel fibre-reinforced concrete with natural aggregates was found to reasonably predict the compressive stress-strain behaviour for steel fibres-reinforced concrete with recycled aggregate.

Lime-cement concrete (LCC) is a non-structural concrete in which lime and cement are used as the main binders. However, although LCC has many applications in reducing the settlement of foundations and providing a support layer for shallow foundations, little research has been conducted to evaluate its behaviour in various moisture conditions. Previous researchers have studied the feasibility of using waste tires in conventional concrete to alleviate their negative environmental impacts. However, in field projects, rubber has not been widely used because its application leads to the strength reduction of concrete. In the case of LCC, attaining high strengths is not required and thus application of waste tire particles sounds reasonable. This research evaluated the impact of various rubber powder contents on the fresh, geotechnical and durability properties of LCC at different saturation degrees induced by the capillary action and groundwater level increment, which has not been studied before. The results of more than 320 tests showed that the application of tire powder increases workability and decreases the water absorption of LCC. Moreover, all 60-day cured specimens exposed to 100% saturation degree experienced a strength reduction of less than 10% by using rubber powder contents varying from 0 to 20%. Moreover, increasing the saturation degree from 0 to 100% decreased the average compressive strength by 13.5 and 22% for 60-day cured samples of two different mix designs. The results of this research confirm that LCC containing up to 10% rubber powder could be promisingly used underneath or close to the groundwater table without its strength and geotechnical properties being jeopardized due to rubber employment and/or exposure to ground moisture.

To provide sustainable reinforced concrete deep beams, the replacement of steel rebars by FRP rebars with high-chemical resistance is proposed by researchers. However, the effects of the concrete strength, top and web longitudinal reinforcements, and types of FRP flexural rebars on the non-linear performance of concrete deep beams have rarely been evaluated. This study numerically assessed the effects of the top and web longitudinal reinforcements and concrete strength on the non-linear behaviour of GFRP- and CFRP-strengthened concrete deep beams with various shear span-to-overall depth (a/h) ratios. As per the results, the highest tensile stress was obtained for the steel reinforcement, and the tensile stress in the CFRP reinforcement was more than that of the GFRP reinforcement under the failure load. Meanwhile, the results of high- and normal-strength concrete deep beams with the web reinforcement (16.4%) were lower than those without the web reinforcement (22.3%). Therefore, the web reinforcement moderately compensated for the low strength of normal concrete and the absence of the top longitudinal rebar to reinforce concrete deep beams in carrying the ultimate load. Furthermore, the participation of the GFRP reinforcement with the high-strength concrete was more than that with the normal-strength concrete in carrying a higher amount of loading.