Supramolecular polymer networks are materials crosslinked by reversible supramolecular interactions, such as hydrogen bonding or electrostatic interactions. Supramolecular materials show very interesting and useful properties resulting from their dynamic nature, such as self-healing, stimuli-responsiveness and adaptability. Here we will discuss recent progress in polymer-based supramolecular networks for the formation of hydrogels and bulk materials.

No abstract

The salt-induced disintegration of lysozyme-filled polyelectrolyte complex micelles, consisting of positively charged homopolymers (PDMAEMA150), negatively charged diblock copolymers (PAA42-PAAm417), and lysozyme, has been studied with dynamic light scattering (DLS) and small-angle neutron scattering (SANS). These measurements show that, from 0 to 0.2 M NaCl, both the hydrodynamic radius (Rh) and the core radius (Rcore) decrease with increasing salt concentration. This suggests that the micellar structures rearrange. Moreover, from approximately 0.2 to 0.4 M NaCl the light-scattering intensity is constant. In this salt interval, the hydrodynamic radius increases, has a maximum at 0.3 M NaCl, and subsequently decreases. This behavior is observed in both a lysozyme-containing system and a system without lysozyme. The SANS measurements on the lysozyme-filled micelles do not show increased intensity or a larger core radius at 0.3 M NaCl. This indicates that from 0.2 to 0.4 M NaCl another structure is formed, consisting of just the diblock copolymer and the homopolymer, because at 0.12 M NaCl the lysozyme-PAA42-PAAm417 complex has disintegrated. One may expect that the driving force for the formation of the complex in this salt range is other than electrostatic.