In this article, an attempt was made to determine the effect of dynamic load on the austempered ductile iron resistance obtained under different conditions of heat treatment. Tests were carried out on six types of cylindrical ductile iron samples austempered at 320, 370 and 400• C for 30 and 180 minutes. For each type of material, two samples were collected. As a next step in the investigations, the samples were subjected to a Taylor impact test. The samples after striking a non-deformable, rigid target were deformed on their front face. After Taylor test, a series of material tests was performed on these samples, noting a significant increase of hardness in the deformed part. This was particularly well visible in the ductile iron isothermally quenched at higher temperatures of 370 and 400• C. In the zone of sample deformation, an increase in the content of ferromagnetic phase was also reported, thus indicating the occurrence of martensitic transformation in the microstructure containing mechanically unstable austenite. A significant amount of deformed graphite was also observed, which was a symptom of the deformation process taking place in samples. The ductile iron was characterized by high toughness and high resistance to the effect of dynamic loads, especially as regards the grade treated at a temperature of 370• C. Keywords: austempered ductile iron, metastable austenite, dynamic deformation, Taylor test W artykule podjęto próbę określenia wpływu obciążeń dynamicznych na odporność żeliwa sferoidalnego ausferrytycznego otrzymanego w różnych warunkach obróbki cieplnej. Badania przeprowadzono dla 6 rodzajów próbek cylindrycznych wykonanych z żeliwa i poddanych hartowaniu izotermicznemu w temperaturze 320, 370 i 400• C w czasie 30 i 180 minut. Dla każdego rodzaju materiału pobrano po dwie próbki, a następnie poddano je uderzeniowemu testowi Taylor'a. Próbki te, po uderzeniu w nieodkształcalną, sztywną płytę zostały czołowo zdeformowane. Wykonano szereg badań materiałowych, stwierdzając znaczne zwiększenie twardości w części odkształconej materiału. Dotyczyło to zwłaszcza żeliwa hartowanego izotermicznie w temperaturach: 370 i 400• C. Wyznaczono również przyrost fazy ferromagnetycznej w strefie odkształconej próbki, co może świadczyć o zachodzeniu przemiany martenzytycznej w mikrostrukturze zawierającej niestabilny mechanicznie austenit. Stwierdzono również obecność znacznej ilości zdeformowanego grafitu, który był wyznacznikiem zachodzenia procesu deformacji próbek. Stwierdzono dużą plastyczność żeliwa oraz jego wysoką odporność na dynamiczne obciążenia, zwłaszcza dla gatunków hartowanych izotermicznie w temperaturze 370• C.

The paper concerns modelling the dynamics of the contact system of the tested sample with an elastic half-space (anvil) during their collision. The original elements in the paper include the proposed general approach to solving the problem of contact dynamics. The presented approach consists in determining the force of impact on the sample during the collision and the joint solution of the problem for the tested sample and the problem for an elastic semi-space under the conditions of the assumptions of Hertz’s theory. The resulting interaction forces allow the determination of displacements and stresses.

The paper presents results of strength tests for tungsten heavy alloys (WHA) designated for the rods of APFSDS–T kinetic projectiles. The strength tests of WHA materials were carried out in conditions of heavy dynamical loads i.e. by the firing. The paper gives a theoretical concept for the identification of stresses within the critical cross-sections of the investigated projectile, and a description of a testing stand which was specially prepared and equipped with 30 mm smooth bore ballistic barrel, and description of methodology and test results. It was especially interesting to test the material against various dynamical loads originating both from the forces of gas pressure and the crosswise forces occurring at the projectile’s move in the barrel.

No abstract

Materiały inżynierskie wykorzystywane w licznych zastosowaniach, w szczególności w motoryzacyjnych i wojskowych, muszą sprostać nowym wymaganiom, z których jednym z najważniejszych jest odporność na obciążenia dynamiczne. Ponieważ zjawiska związane z takimi interakcjami są dość złożone, stosuje się niestatyczne typy testów do oceny i porównania różnych potencjalnych materiałów. W pracy tej dwa rodzaje żeliwa ADI wytworzono w różnych warunkach austenityzowania i hartowania, otrzymując różną morfologię ausferrytu. Próbki z obu materiałów były poddawane różnym dynamicznym szybkościom odkształcania. Oceniono odporność na martenzytyczną przemianę odkształceniową w zależności od mikrostruktury i szybkości odkształcania. Badania XRD i LM były wykorzystane do oceny właściwości oraz wpływu dużych szybkości odkształcania na strukturę materiału. Słowa kluczowe: żeliwo sferoidalne ausferrytyczne, test Taylora, odporność na obciążenia dynamiczne, przemiana odkształceniowa 1 Autor do korespondencji/corresponding author: Dawid Myszka Politechnika Warszawska,