Using precious metals as plating materials is an effective measure to avoid failures of electrical contacts caused by fretting. When using precious metals, such as gold, one of the limitations to their lifetime is the wear resistance. In order to improve the wear resistance of gold plates, gold alloy is usually used. Instead of alloying elements, nanoscale particles of metal oxides were used for the modification of plates in our investigation. Some of the nanoscale particles show considerable impact on the performance of plates for electrical contacts. This paper shows the first results and new challenges when using nanoscale particles for electroplating.

The effect of La on Al/NaBH4 hydrolysis was elaborated in the present paper. Hydrogen generation amount increases but hydrogen generation rate decreases with La content increasing. There is an optimized composition that Al-15 wt% La-5 wt% NiCl2/NaBH4 mixture (Al-15 wt% La-5 wt% NiCl2/NaBH4 weight ratio, 1 : 3) has 126 mL g−1 min−1 maximum hydrogen generation rate and 1764 mL g−1 hydrogen generation amount within 60 min. The efficiency is 88%. Combined with NiCl2, La has great effect on NaBH4 hydrolysis but has little effect on Al hydrolysis. Increasing La content is helpful to decrease the particle size of Al-La-NiCl2 in the milling process, which induces that the hydrolysis byproduct Ni2B is highly distributed into Al(OH)3 and the catalytic reactivity of Ni2B/Al(OH)3 is increased therefore. But hydrolysis byproduct La(OH)3 deposits on Al surface and leads to some side effect. The Al-La-NiCl2/NaBH4 mixture has good stability in low temperature and its hydrolytic performance can be improved with increasing global temperature. Therefore, the mixture has good safety and can be applied as on board hydrogen generation material.