The main basic ingredients needed for the manufacture of this geopolymer material are materials that contain a lot of silica and aluminia elements. The 1st stage test was carried out to determine the geopolymer paste with the maximum compressive strength at the ratio of NaOH to Na2SiO3 of 1; 1.5; 2; 2.5. The second stage of testing was carried out using a geopolymer paste with the highest compressive strength, namely the ratio of NaOH to Na2SiO3 of 2.5 with a compressive strength of 22.56 MPa. Based on the results of the compressive strength test, the maximum compressive strength at the age of 28 days is 7.64 MPa. The results of the compressive strength of concrete are much lower than the compressive strength of the paste, it shows that the paste does not bind too much with the aggregate. This is evidenced by the results of the compressive strength of conventional concrete which is much higher than that of geopolymer concrete using the same aggregate. With the results of the maximum compressive strength at the age of 28 days is 29.51 MPa.

Beton salah satu material konturuksi mampu memikul beban tekan, tetapi lemah dalam menerima beban tarik. Hal ini menyebabkan beton bersifat getas dan dapat. mengakibatkan keruntuhan mendadak sehingga serat digunakan pada beton. Tetapi bukan berarti beton tidak mengalami keruntuhan tarik. Dengan penambahan serat pelepah kelapa sawit yang merupakan bahan lokal, diharapkan dapat memperbaiki kelemahan beton. Variasi kadar atau presentase serat kelapa sawit yang ditambahkan ke dalam campuran beton adalah sebesar 1%, 1,5% dan 2% dari total berat semen beton silinder.  Hasil Penelitian kuat tekan, penambahan dan semakin besar l/d serat pelepah kelapa sawit tidak memberikan pengaruh yang signifikan terhadap peningkatan kuat tekan, kuat tekan tertinggi di peroleh pada rasio l/d = 50 dengan kadar serat 1% dengan nilai kuat tekan sebesar 14,33 MPa. Pada Pengujian kuat tarik belah beton tertinggi pada kadar serat 1% dengan rasio l/d = 50 nilai kuat tarik yang dihasilkan sebesar 2,10 MPa pada umur 7 hari. Kata kunci: beton serat, kuat tekan, pelepah kelapa sawit, kuat tarik belah