Blends of soy protein (SP) and a semicrystalline polylactide (PLA) were prepared using a twin-screw extruder. The melt rheology, phase morphology, mechanical properties, water resistance, and thermal and dynamic mechanical properties were investigated on specimens prepared by injection molding of these blends. The melt flowability of soy-based plastics was improved through blending with PLA. Scanning electron microscopy revealed that a cocontinuous phase structure existed in the blends with soy protein concentrate (SPC) to PLA ratios ranging from 30:70 to 70:30. SPC/PLA blends showed fine co-continuous phase structures, while soy protein isolate (SPI)/ PLA blends presented severe phase coarsening. At the same SP to PLA ratios, SPC/PLA blends demonstrated a higher tensile strength than SPI/PLA blends. The water absorption of soy plastics was greatly reduced by blending with PLA. The compatibility was improved by adding 1-5 phr poly(2-ethyl-2-oxazoline) (PEOX) in the blends, and the resulting blends showed an obvious increase in tensile strength and a reduction in water absorption for SPI/PLA blends. The compatibility between SP and PLA was evaluated by mechanical testing, dynamic mechanical analysis (DMA), water absorption, and scanning electron microscopy (SEM) experiments. Differential scanning calorimetry (DSC) revealed that PLA in the blends was mostly amorphous in the injection molded articles, and SP accelerated the cold crystallization and could increase the final crystallinity of PLA in the blends. Blends of soy protein (SP) and a semicrystalline polylactide (PLA) were prepared using a twin-screw extruder. The melt rheology, phase morphology, mechanical properties, water resistance, and thermal and dynamic mechanical properties were investigated on specimens prepared by injection molding of these blends. The melt flowability of soy-based plastics was improved through blending with PLA. Scanning electron microscopy revealed that a cocontinuous phase structure existed in the blends with soy protein concentrate (SPC) to PLA ratios ranging from 30:70 to 70:30. SPC/PLA blends showed fine co-continuous phase structures, while soy protein isolate (SPI)/ PLA blends presented severe phase coarsening. At the same SP to PLA ratios, SPC/PLA blends demonstrated a higher tensile strength than SPI/PLA blends. The water absorption of soy plastics was greatly reduced by blending with PLA. The compatibility was improved by adding 1-5 phr poly(2-ethyl-2-oxazoline) (PEOX) in the blends, and the resulting blends showed an obvious increase in tensile strength and a reduction in water absorption for SPI/PLA blends. The compatibility between SP and PLA was evaluated by mechanical testing, dynamic mechanical analysis (DMA), water absorption, and scanning electron microscopy (SEM) experiments. Differential scanning calorimetry (DSC) revealed that PLA in the blends was mostly amorphous in the injection molded articles, and SP accelerated the cold crystallization and could increase the final crystallinity of PLA in the blen...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.