Adhesive hydrogels are widely applied for biological and medical purposes; however, they are generally unable to adhere to tissues under wet/underwater conditions. Herein, described is a class of novel dynamic hydrogels that shows repeatable and long‐term stable underwater adhesion to various substrates including wet biological tissues. The hydrogels have Fe3+‐induced hydrophobic surfaces, which are dynamic and can undergo a self‐hydrophobization process to achieve strong underwater adhesion to a diverse range of dried/wet substrates without the need for additional processes or reagents. It is also demonstrated that the hydrogels can directly adhere to biological tissues in the presence of under sweat, blood, or body fluid exposure, and that the adhesion is compatible with in vivo dynamic movements. This study provides a novel strategy for fabricating underwater adhesive hydrogels for many applications, such as soft robots, wearable devices, tissue adhesives, and wound dressings.

Localized inclusions of liquids provide solid materials with many functions, such as self-healing, secretion, and tunable mechanical properties, in a spatially controlled mode. However, a strategy to control the distribution of liquid droplets in solid matrices directly obtained from a homogeneous solution has not been reported thus far. Herein, we describe an approach to selectively localize liquid droplets in a supramolecular gel directly obtained from its solution by using evaporative lithography. In this process, the formation of droplet-embedded domains occurs in regions of free evaporation where the non-volatile liquid is concentrated and undergoes a phase separation to create liquid droplets prior to gelation, while a homogeneous gel matrix is formed in the regions of hindered evaporation. The different regions of a coating with droplet embedment patterns display different secretion abilities, enabling the control of the directional movement of water droplets.

Influence of plasma-generated negative oxygen ion impingement on magnetron sputtered amorphous SiO 2 thin films during growth at low temperatures

This study reports on a facile and widely applicable method of transferring chemical vapor deposited (CVD) graphene uniformly onto optically transparent and mechanically flexible substrates using commercially available, low-cost ultraviolet adhesive (UVA) and hot-press lamination (HPL). We report on the adhesion potential between the graphene and the substrate, and we compare these findings with those of the more commonly used cast polymer handler transfer processes. Graphene transferred with the two proposed methods showed lower surface energy and displayed a higher degree of adhesion (UVA: 4.40 ± 1.09 N/m, HPL: 0.60 ± 0.26 N/m) compared to equivalent CVD-graphene transferred using conventional poly(methyl methacrylate) (PMMA: 0.44 ± 0.06 N/m). The mechanical robustness of the transferred graphene was investigated by measuring the differential resistance as a function of bend angle and repeated bend-relax cycles across a range of bend radii. At a bend angle of 100° and a 2.5 mm bend radius, for both transfer techniques, the normalized resistance of graphene transferred on polyethylene terephthalate (PET) was around 80 times less than that of indium-tin oxide on PET. After 10(4) bend cycles, the resistance of the transferred graphene on PET using UVA and HPL was found to be, on average, around 25.5 and 8.1% higher than that of PMMA-transferred graphene, indicating that UVA- and HPL-transferred graphene are more strongly adhered compared to PMMA-transferred graphene. The robustness, in terms of maintained electrical performance upon mechanical fatigue, of the transferred graphene was around 60 times improved over ITO/PET upon many thousands of repeated bending stress cycles. On the basis of present production methods, the development of the next-generation of highly conformal, diverse form factor electronics, exploiting the emerging family of two-dimensional materials, necessitates the development of simple, low-cost, and mechanically robust transfer processes; the developed UVA and HPL approaches show significant potential and allow for large-area-compatible, near-room temperature transfer of graphene onto a diverse range of polymeric supports.