Chromium deposits rank among the most widespread metal coatings for functional and decorative purposes. However, electrodeposition from Cr(VI) aqueous solution, which is the industrial process currently used to achieve thin chromium deposits, presents several environmental issues, urging the development of alternative solutions. In this study, which aims to compare the functional and aesthetical properties of decorative coatings, 800 nm thick chromium layers were deposited directly onto copper substrates by means of magnetron sputtering (MS) and direct current electrodeposition (ED). The obtained coatings were characterized regarding their thickness, morphology, color index, chemical composition, and corrosion resistance viewpoints. With respect to the electroplated samples, which constitute the benchmark, the magnetron sputtered ones appeared to be darker but showed a pleasing reflective appearance and superior thickness homogeneity, as well as the absence of voids and macrocracks, as evidenced by scanning electron microscopy (SEM) investigation. Regarding the anticorrosion performances of the chromium layers, electrochemical and standard salt spray test (NSS test) were carried out at room temperature in 3.5% NaCl solution, and evidenced similar, if not better, results for the magnetron sputtered coatings. On the whole, the data displayed here demonstrates the suitability of magnetron sputtering technology for use as an industrially feasible finishing technology for both aesthetic and mild-condition anticorrosion purposes.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.