The keyhole mode in laser powder bed fusion (LPBF) additive manufacturing can be associated with excessive porosity and spatter, however, the underlying physics in multilayer build conditions remain unclear.Here, we used ultra-fast synchrotron X-ray imaging to reveal this phenomena. We revealed melt pool dynamics, keyhole porosity and spatter formation mechanisms and their impact in all layers of the build. We observed that the transient melt pool dynamics associated with the keyhole include: (I) keyhole initiation, (II) keyhole development, and (III) melt pool recovery. Porosity and spatter were associated with stages (II) and (III). We also discovered that droplet spatter can form due to the collapse of the keyhole recoil zone, causing molten particle agglomeration and ejection during stage (III). Our results clarify the transient dynamics behind the keyhole mode in a multi-layer LBPF process and can be used to guide the reduction in porosity and spatter in additive manufacturing.
Porosity and high surface roughness can be detrimental to the mechanical performance of laser powder bed fusion (LPBF) additive manufactured components, potentially resulting in reduced component life. However, the link between powder layer thickness on pore formation and surface undulations in the LPBF parts remains unclear. In this paper, the influence of processing parameters on Ti-6Al-4V additive manufactured thin-wall components are investigated for multilayer builds, using a custom-built process replicator and in situ highspeed synchrotron X-ray imaging. In addition to the formation of initial keyhole pores, the results reveal three pore phenomena in multilayer builds resulting from keyhole melting: (i) healing of the previous layers pores via liquid filling during remelting; (ii) insufficient laser penetration depth to remelt and heal pores; and (iii) pores formed by keyholing which merge with existing pores, increasing the pore size. The results also show that the variation of powder layer thickness influences which pore formation mechanisms take place in multilayer builds.High-resolution X-ray computed tomography images reveal that clusters of pores form at the ends of tracks and when variations in the layer thickness and melt flow cause irregular 2 remelting and track height undulations. Extreme variations in height were found to lead to lack of fusion pores in the trough regions. It is hypothesised that the end of track pores were augmented by soluble gas which is partitioned into the melt pool and swept to track ends, supersaturating during end of track solidification and diffusing into pores increasing their size.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.