Abstract. Reinforced concrete (RC) structures are gradually being degraded all over the world, largely due to corrosion of the embedded steel bars caused by an attack of chloride penetration. Initial curing would be regarded as one factor influencing chloride diffusion in concrete in combination with cover cracking that is also of great attention for reinforced structures. In this study, a non-steady state diffusion test of chloride ion involving RC beam specimens with a water-to-cement ratio of 0.5, initial curing temperatures of 5°C or 20°C and three types of crack widths ranging from 0 to 0.2mm was performed. Chloride content at 5°C or was determined. The results show that the higher chloride content was obtained in condition of crack width large than 0.1mm with low initial curing temperature and there are no obvious differences in chloride content when the crack width was not larger than 0.1mm.
Reinforced concrete (RC) structures are gradually being degraded all over the world, largely due to corrosion of the embedded steel bars caused by an attack of chloride penetration. Initial curing would be regarded as one factor influencing chloride diffusion in concrete in combination with cover cracking that is also of great attention for reinforced structures. In this study, a non-steady state diffusion test of chloride ion involving RC beam specimens with a water-to-cement ratio of 0.5, initial curing temperatures of 5°C or 20°C and three types of crack widths ranging from 0 to 0.2mm was performed. Chloride content at 5°C or was determined. The results show that the higher chloride content was obtained in condition of crack width large than 0.1mm with low initial curing temperature and there are no obvious differences in chloride content when the crack width was not larger than 0.1mm.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.