This study investigated the capability of honeycomb core structures made of kenaf fibre-reinforced polylactic acid (PLA) composite. Two types of kenaf fibre were used in this study, these being woven kenaf and non-woven cotton/kenaf. Initially, the corrugated shape panel was manufactured using a hot moulding compression method. The panel was then cut into corrugated strips, bonded together using epoxy resin to form the honeycomb core structure, and balsa wood used as their skins. The effects of core height and crosshead displacement rate were investigated. The honeycomb core consisted of 20 mm, 30 mm and 40 mm core heights, and the crosshead displacement rate ranged from 2 mm/min to 500 min/min. Of all the samples, core structure with a height of 20 mm tested at 500 mm/min offered the highest value of compressive strength and specific energy absorption, which were 6.23 MPa and 12.36 kJ/kg, respectively. It was also discovered that the core height and loading rate have significant effects on the mechanical properties of the kenaf/PLA honeycomb core structure.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.