High-temperature processing was used to improve the barrier properties of three sets of n-type 4H-SiC Schottky diodes fabricated with Ni Schottky contacts. We obtained an optimum average barrier height of 1.78 eV and an ideality factor of 1.09 using current-voltage measurements on diodes annealed in vacuum at 500°C for 24 h. Nonannealed contacts had an average barrier height of 1.48 eV and an ideality factor of 1.85. The Rutherford backscattering spectra of the Ni/SiC contacts revealed the formation of a nickel silicide at the interface, accompanied by a substantial reduction in oxygen following annealing.